LEXAN™ XHT1141 resin
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LEXAN™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dLpKoh_LEXANXHT1141resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| XHT1141 is a high flow, high heat polycarbonate copolymer. It is the lowest heat product in the LEXAN XHT portfolio. It is available in a range of opaque and limited transparent colors. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 300°C/1.2 kg | 16.0 | cm³/10min | ISO 1133 |
| 330°C/2.16 kg | 70.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow (3.20 mm) | 0.60 - 0.90 | % | Internal method |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.30 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.30 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2400 | MPa | ISO 527-2/1 |
| Tensile Stress | ISO 527-2/50 | ||
| Yield | 65.0 | MPa | ISO 527-2/50 |
| Fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2/50 | ||
| Yield | 6.5 | % | ISO 527-2/50 |
| Fracture | 80 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2400 | MPa | ISO 178 |
| Flexural Stress | 100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 2 | ISO 179/1eA | ||
| -30°C | 12 | kJ/m² | ISO 179/1eA |
| 23°C | 16 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 3 | ISO 179/1eU | ||
| -30°C | No Break | ISO 179/1eU | |
| 23°C | No Break | ISO 179/1eU | |
| Notched Izod Impact 4 | ISO 180/1A | ||
| -30°C | 10 | kJ/m² | ISO 180/1A |
| 23°C | 14 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 5 | ISO 180/1U | ||
| -30°C | No Break | ISO 180/1U | |
| 23°C | No Break | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 6 | |||
| 0.45 MPa, unannealed, 64.0mm span | 144 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 64.0mm span | 132 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 150 | °C | ISO 306/B50 |
| -- | 152 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.0E-5 | cm/cm/°C | ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 125 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 40 - 60 | % | |
| Rear Temperature | 270 - 305 | °C | |
| Middle Temperature | 280 - 325 | °C | |
| Front Temperature | 290 - 335 | °C | |
| Nozzle Temperature | 285 - 330 | °C | |
| Processing (Melt) Temp | 290 - 335 | °C | |
| Mold Temperature | 85.0 - 130 | °C | |
| Back Pressure | 0.300 - 0.700 | MPa | |
| Screw Speed | 40 - 90 | rpm | |
| Vent Depth | 0.025 - 0.080 | mm |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 80*10*3 sp=62mm |
| 3 . | 80*10*3 sp=62mm |
| 4 . | 80*10*3 |
| 5 . | 80*10*3 |
| 6 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinpolene MBW1444 | Teknor Apex Asia Pacific PTE. LTD. | PP, Unspecified | Sinpolene |
| Monprene® OM-10250-01 | Teknor Apex Company | TPE | Monprene® |
| Triax® 1315 | INEOS ABS (USA) | ABS+Nylon | Triax® |
| New-prene™ 6185N | Total Polymer Vision (Suzhou) Co., LTD | PP+EPDM | New-prene™ |
| Keliren® CM352LF | Hangzhou Keli Chemical Co., Ltd. | CPE | Keliren® |