NORYL™ EN265 resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dLON5Z_NORYL-EN265-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Extrusion grade. 254F (123C) DTUL. UL94 V-1 rated. |
| General Information | |
|---|---|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.08 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 - 0.70 | % | Internal method |
| Water Absorption (24 hr) | 0.070 | % | ASTM D570 |
| Outdoor Suitability | f1 | UL 746C |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield) | 63.4 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 25 | % | ASTM D638 |
| Flexural Modulus 3(100 mm Span) | 2550 | MPa | ASTM D790 |
| Flexural Strength 4(Yield, 100 mm Span) | 99.3 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -40°C | 130 | J/m | ASTM D256 |
| 23°C | 190 | J/m | ASTM D256 |
| Dart Drop Impact | ASTM D3029 | ||
| -40°C | 4.07 | J | ASTM D3029 |
| -30°C | 14.9 | J | ASTM D3029 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 123 | °C | ASTM D648 |
| CLTE - Flow (-40 to 95°C) | 5.9E-5 | cm/cm/°C | ASTM E831 |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (3.20 mm, in Oil) | 20 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 2.69 | ASTM D150 | |
| 60 Hz | 2.69 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 7.0E-4 | ASTM D150 | |
| 60 Hz | 7.0E-4 | ASTM D150 | |
| Arc Resistance 5 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | UL 94 | |
| 5.99 mm | V-0 | UL 94 | |
| Oxygen Index | 29 | % | ASTM D2863 |
| Radiant Panel Listing (UL) | RP100 |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 116 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Cylinder Zone 1 Temp. | 204 | °C | |
| Cylinder Zone 2 Temp. | 204 | °C | |
| Cylinder Zone 3 Temp. | 227 | °C | |
| Cylinder Zone 4 Temp. | 227 | °C | |
| Adapter Temperature | 249 | °C | |
| Melt Temperature | 227 - 254 | °C | |
| Die Temperature | 249 | °C |
| Extrusion instructions |
|---|
| Drying Time (Cumulative): 8 hrs |
| Note Message | |
|---|---|
| 1 . | Type 1, 50mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | 2.6 mm/min |
| 4 . | 2.6 mm/min |
| 5 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SILPURAN® 8461/60 | Wacker Chemie AG | Silicone | SILPURAN® |
| VECTOR® 4113 | Dexco Polymers LP | SIS | VECTOR® |
| AKROTEK® PEEK CF 40 black (5099) | AKRO-PLASTIC GmbH | PEEK | AKROTEK® |
| Geon™ Vinyl Flexible 90057 | PolyOne Corporation | PVC, Flexible | Geon™ Vinyl Flexible |
| LNP™ THERMOCOMP™ RF002 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ THERMOCOMP™ |