ALCUDIA® LDPE 3235FGD
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | REPSOL |
| Trademark: | ALCUDIA® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dLEGGT_ALCUDIA-LDPE-3235FGD.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ALCUDIA® 3235FGD is a low density polyethylene grade, produced by high pressure autoclave technology, suitable for thin blown film or cast film applications. The easy processability of this grade allows high extrusion speeds at low gauges. This material combines easy tear, enhanced toughness and good optical properties. It contains high level of slip (erucamide), antiblock and antioxidant additives. TYPICAL APPLICATIONS
Recommended melt temperature range from 150 to 190°C. Processing conditions should be optimised for each production line. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 0.932 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 3.5 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (vs. Itself - Dynamic, Blown Film) | 0.15 | ISO 8295 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 40 | µm | |
| Tensile Stress | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 23.0 | MPa | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 18.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 40 µm, blown film | 350 | % | ISO 527-3 |
| TD : Broken, 40 µm, blown film | 550 | % | ISO 527-3 |
| Dart Drop Impact (40 µm, Blown Film) | 70 | g | ISO 7765-1 |
| Elmendorf Tear Strength | ISO 6383-2 | ||
| MD : 40 µm, blown film | 1.1 | N | ISO 6383-2 |
| TD : 40 µm, blown film | 2.0 | N | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 107 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (45°, 40.0 µm, Blown Film) | 75 | ASTM D2457 | |
| Haze (40.0 µm, Blown Film) | 7.5 | % | ASTM D1003 |
| Additional Information |
|---|
| Data taken from 40 µm thickness film, blow up ratio 2.5:1. |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Melt Temperature | 150 - 190 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MALAT 37G300 - 1417 | AD majoris | PBT | MALAT |
| THERMOLAST® K TF8TAA (Series: FC/AD1/ht) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Bapolene® HD2032 | Bamberger Polymers, Inc. | HDPE | Bapolene® |
| alphalon™ E 40 LN | Grupa Azoty ATT Polymers GmbH | Nylon 6 | alphalon™ |
| LG PMMA EG920B | LG MMA Corp. | Acrylic (PMMA) | LG PMMA |