Zytel® RS LC1000 BK385
| Category: | Nylon 1010 , RENEWABLY SOURCED™ POLYAMIDES* |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® RS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dKu8Z5_Zytel-RS-LC1000-BK385.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UV Stabilized, Renewably Sourced, Polyamide 1010 Developed for Extrusion |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Part Marking Code (ISO 11469) |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.05 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.80 | -- | % | |
| Flow | 1.4 | -- | % | |
| Water Absorption (Equilibrium, 23°C, 2.00 mm, 50% RH) | 1.0 | -- | % | ISO 62 |
| Viscosity Number | 130 | -- | cm³/g | ISO 307 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 2100 | 1160 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 60.0 | 49.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield) | 4.6 | 24 | % | ISO 527-2 |
| Nominal Tensile Strain at Break | 50 | > 50 | % | ISO 527-2 |
| Flexural Modulus | 1740 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 8.0 | 5.0 | kJ/m² | |
| 23°C | 5.0 | 10 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Melting Temperature 1 | 203 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.1E-4 | -- | cm/cm/°C | |
| Transverse | 1.2E-4 | -- | cm/cm/°C |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 1.50 mm | HB | -- | ||
| 3.00 mm | HB | -- |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen RP320M | LyondellBasell Industries | PP Random Copolymer | Moplen |
| Braskem PE GM5240PR | Braskem | HDPE | Braskem PE |
| LUVOCOM® 1105/GN7348 | Lehmann & Voss & Co. | PEEK | LUVOCOM® |
| Petrothene® GA601033 | LyondellBasell Industries | LLDPE | Petrothene® |
| LNP™ THERMOCOMP™ MX85738 compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |