Order Products : sales@su-jiao.com
TARFLON™ AC1070C
| Category: | PC , Polycarbonate |
| Manufacturer: | Idemitsu Kosan Co., Ltd. |
| Trademark: | TARFLON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dIQ8OL_TARFLON-AC1070C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flame retardant agent free, High flow |
| General Information | |
|---|---|
| Features |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.22 | g/cm³ | ISO 1183 |
| Melt Volume-Flow Rate (MVR) (280°C/2.16 kg) | 21.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 2.00 mm | 0.50 to 0.70 | % | |
| Flow : 2.00 mm | 0.50 to 0.70 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break | 80 | % | ISO 527-2 |
| Flexural Modulus | 2900 | MPa | ISO 178 |
| Flexural Stress | 93.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 40 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 130 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 116 | °C | ISO 75-2/A |
| RTI Elec | 80.0 | °C | UL 746 |
| RTI Imp | 80.0 | °C | UL 746 |
| RTI Str | 80.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | V-1 | ||
| 2.00 mm | V-0 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| ISO Shortname | >PC< |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 5.0 to 8.0 | hr | |
| Rear Temperature | 260 to 280 | °C | |
| Middle Temperature | 260 to 280 | °C | |
| Front Temperature | 260 to 280 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® C200MN | Reliance Industries Limited | PP Impact Copolymer | REPOL® |
| Tarnamid® T- 27 MT 40 | Grupa Azoty S.A. | Nylon 6 | Tarnamid® |
| XENOY™ 1760 resin | SABIC Innovative Plastics Asia Pacific | PC+PBT | XENOY™ |
| AGILITY™ 2001 | The Dow Chemical Company | LDPE | AGILITY™ |
| LNP™ STAT-KON™ ME003S compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ STAT-KON™ |