LNP™ STAT-KON™ AE008XXY compound
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dIISsE_LNP-STAT-KON-AE008XXY-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON AE008XXY is a compound based on ABS resin containing 40% Carbon Fiber. Added feature of this material ia: Electrically Conductive. Also known as: LNP* STAT-KON* Compound AE008XXY Product reorder name: AE008XXY |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.30 | % | |
| Across Flow : 24 hr | 0.30 to 0.50 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.17 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.24 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 30100 | MPa | ASTM D638 |
| -- | 25300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 143 | MPa | ASTM D638 |
| Break | 141 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 0.90 | % | ASTM D638 |
| Break | 0.90 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 23700 | MPa | ASTM D790 |
| -- 5 | 24700 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 215 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 59 | J/m | ASTM D256 |
| 23°C 7 | 5.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 320 | J/m | ASTM D4812 |
| 23°C 8 | 18 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 6.00 | J | ASTM D3763 |
| -- | 2.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 106 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 107 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 101 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 101 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 2.1E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 2.5E-5 | cm/cm/°C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 2.0 to 6.0 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.050 to 0.10 | % | |
| Rear Temperature | 204 to 216 | °C | |
| Middle Temperature | 232 to 243 | °C | |
| Front Temperature | 266 to 277 | °C | |
| Processing (Melt) Temp | 260 | °C | |
| Mold Temperature | 71.1 to 82.2 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 101 SP (20% FOAMED) | RTP Company | PP, Unspecified | RTP |
| CP PRYME® Nylon 66 NN200L | Chase Plastics Services Inc. | Nylon 66 | CP PRYME® Nylon 66 |
| Huafon JF-P-4170 / JF-I-4118 (outsole) | Huafon Group Co., Ltd. | PUR-Ester | Huafon |
| IROSTIC® S 7730 | Huntsman Corporation | TPU, Unspecified | IROSTIC® |
| LEXAN™ XHT3141 resin | SABIC Innovative Plastics | PC | LEXAN™ |