DILAMID® 66 FVT 30 NAT A
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Dilaplast S.p.A. |
| Trademark: | DILAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dI06nW_DILAMID-66-FVT-30-NAT-A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| DILAMID®66 FVT 30 NAT A is a polyamide 66 (nylon 66) material that contains a 30% glass fiber reinforced material. This product is available in Europe, and the processing method is injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.37 | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.40 - 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 120 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.5 | % | ISO 527-2 |
| Flexural Modulus | 6.50 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 6.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 220 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 220 | °C | ISO 306/B50 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 20 | kV/mm | ASTM D149 |
| Comparative Tracking Index | 500 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature (2.00 mm) | 650 | °C | IEC 60695-2-13 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 70.0 - 100 | °C | |
| Drying Time | 2.0 - 8.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 - 300 | °C | |
| Middle Temperature | 270 - 310 | °C | |
| Front Temperature | 280 - 320 | °C | |
| Nozzle Temperature | 270 - 310 | °C | |
| Processing (Melt) Temp | 280 - 320 | °C | |
| Mold Temperature | 70.0 - 110 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shin-Etsu Elastomer SFX-14036AU | Shin-Etsu Silicones of America | Fluoro Si | Shin-Etsu Elastomer |
| ExxonMobil™ PP1063L1 | ExxonMobil Chemical | PP Homopolymer | ExxonMobil™ |
| Larpeek 10 G/15 | LATI S.p.A. | PEEK | Larpeek |
| LNP™ LUBRICOMP™ OCL36 compound | SABIC Innovative Plastics | PPS, Linear | LNP™ LUBRICOMP™ |
| Kepamid® 1325GVS | Korea Engineering Plastics Co., Ltd | Nylon 6 | Kepamid® |