Plantic® R1
| Category: | Biodeg Polymers , Biodegradable Polymers |
| Manufacturer: | Plantic Technologies Limited |
| Trademark: | Plantic® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dHzyGZ_Plantic-R1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Plantic Technologies Limited develops and produces advanced bio-based materials. Plantic® is an innovative product made from corn-starch (maize) that is Australian grown and non-genetically modified. Plantic® is an Australian registered trademark of Plantic Technologies Limited. Plantic® R1 is an advanced technology sheet manufactured from corn starch that is fully biodegradable and compostable. Plantic® R1 is suitable for thermoforming applications (e.g. for packing foods & goods with water activity of 35% to 70%). Also suitable for direct contact with fatty foods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.35 to 1.45 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.0 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.17 | ||
| vs. Itself - Static | 0.22 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 250 | µm | |
| Secant Modulus - MD (250 µm) | 2200 to 2400 | MPa | ASTM D882 |
| Tensile Strength - MD (Yield, 250 µm) | 42.0 to 46.0 | MPa | ASTM D882 |
| Tensile Elongation - MD (Break, 250 µm) | 20 to 36 | % | ASTM D882 |
| Elmendorf Tear Strength - MD (250 µm) | 3500 to 5500 | g | ASTM D1922 |
| Oxygen Permeability 1(38°C, 250 µm) | 0.130 | cm³/m²/24 hr | ASTM D1434 |
| Water Vapor Transmission 2 | 35 to 40 | g/m²/24 hr | ASTM E96 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glass Transition Temperature | 40.0 to 45.0 | °C | ASTM E1356 |
| Vicat Softening Temperature | 130 to 135 | °C | ASTM D1525 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss (60°, 250 µm) | 80 to 85 | ASTM D2457 | |
| Transmittance (250 µm) | 89.0 to 93.0 | % | ASTM D1003 |
| Haze (250 µm) | 15 to 20 | % | ASTM D1003 |
| Additional Information | Nominal Value | Test Method | |
|---|---|---|---|
| Water Activity 3 | 0.500 to 0.650 | Internal Method |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 38°C, 50%RH |
| 3 . | PTM 03 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mirakutoran® TPU E885 | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Hifax CA 1110 A3-LS | LyondellBasell Industries | Polyolefin, Unspecified | Hifax |
| HiFill® TPU/I GF25 | Techmer Engineered Solutions | TPU-Polyether | HiFill® |
| ALCOM® PA66 910/7 GF25 MR15 | ALBIS PLASTIC GmbH | Nylon 66 | ALCOM® PA66 |
| LNP™ STAT-KON™ OE008A compound | SABIC Innovative Plastics Europe | PPS, Branched | LNP™ STAT-KON™ |