TECHNYL® C 52G2 MV25 GREY G 1783 CF Datasheet,Nylon 6,Solvay Engineering Plastics-SHANGHAI SUSHENG

Message
TECHNYL® C 52G2 MV25 Grey G 1783 CF is a Non-phosphorous and Non-halogenated flame retardant polyamide 6, reinforced with 25% of mixed glass fibre and mineral filler, heat stabilized, for injection moulding. This flame retardant grade offers a low smoke toxicity, a high glow- wire resistance and good all round mechanical properties

General Information
Filler / Reinforcement	Glass \mineral, 25% filler by weight
Additive	heat stabilizer Flame retardancy
Features	Anti-arc Phosphorus content, low (to none) Halogen-free
Uses	Electrical/Electronic Applications
Agency Ratings	EC 1907/2006 (REACH) UL QMFZ2
Appearance	Grey Natural color
Forms	Particle
Processing Method	Injection molding
Resin ID (ISO 1043)	PA6-(MD+GF)25 FR(30)

Physical	Dry	Conditioned	Unit	Test Method
Density	1.37	--	g/cm³	ISO 1183/A
Water Absorption (23°C, 24 hr)	1.1	--	%	ISO 62

Mechanical	Dry	Conditioned	Unit	Test Method
Tensile Modulus (23°C)	8100	3500	MPa	ISO 527-2/1A
Tensile Stress (Break, 23°C)	105	53.0	MPa	ISO 527-2/1A
Tensile Strain (Break, 23°C)	2.4	--	%	ISO 527-2

Impact	Dry	Conditioned	Unit	Test Method
Charpy Notched Impact Strength (23°C)	4.0	7.0	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength (23°C)	43	75	kJ/m²	ISO 179/1eU
Notched Izod Impact (23°C)	4.6	8.2	kJ/m²	ISO 180

Thermal	Dry	Conditioned	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	215	--	°C	ISO 75-2/Bf
1.8 MPa, not annealed	190	--	°C	ISO 75-2/Af
Melting Temperature	222	--	°C	ISO 11357-3

Electrical	Dry	Conditioned	Unit	Test Method
Comparative Tracking Index (Solution A)	500	--	V	IEC 60112

Flammability	Dry	Conditioned	Unit	Test Method
Flame Rating				UL 94
0.8 mm	V-2	--		UL 94
1.6 mm	V-2	--		UL 94
3.2 mm	V-2	--		UL 94
Glow Wire Flammability Index				IEC 60695-2-12
1.6 mm	960	--	°C	IEC 60695-2-12
3.2 mm	960	--	°C	IEC 60695-2-12
Oxygen Index	31	--	%	ISO 4589-2

Injection	Dry	Unit
Drying Temperature	80	°C
Suggested Max Moisture	0.20	%
Rear Temperature	230 - 235	°C
Middle Temperature	235 - 240	°C
Front Temperature	235 - 245	°C
Mold Temperature	60 - 90	°C

Injection instructions
The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: All reinforced flame retardant compounds generate some level of abrasion/corrosion to the steel processing equipment. These issues can be worsened by using incorrect processing conditions (temperatures, residence time, moisture level ...) during the moulding process. Therefore, Solvay recommends to use the advised processing conditions detailed in this technical data sheet. For equipment that comes into contact with molten flame retarded compounds, Solvay advises to use a steel containing high chromium & high carbon content (minimum concentration of 16% Chromium) to prevent corrosion and abrasion. For the correct reference of steel associated to flame retardant compounds processing, please refer to your equipment manufacturers. For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature at 120°C. Of course it should be noted that this improvement in the surface appearance may be at the expense of the cycle time.

Injection instructions

The material is supplied in airtight bags, ready for use. In case that the virgin material has absorbed moisture, it must be dried with a dehumidified air drying equipment, dew point mini -20°C. Recommended time 2-4hInjection Advice: All reinforced flame retardant compounds generate some level of abrasion/corrosion to the steel processing equipment. These issues can be worsened by using incorrect processing conditions (temperatures, residence time, moisture level ...) during the moulding process. Therefore, Solvay recommends to use the advised processing conditions detailed in this technical data sheet. For equipment that comes into contact with molten flame retarded compounds, Solvay advises to use a steel containing high chromium & high carbon content (minimum concentration of 16% Chromium) to prevent corrosion and abrasion. For the correct reference of steel associated to flame retardant compounds processing, please refer to your equipment manufacturers. For Mould Temperature, in the case of parts where the surface roughness is required we can recommend a temperature at 120°C. Of course it should be noted that this improvement in the surface appearance may be at the expense of the cycle time.

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Solvay Engineering Plastics
Trademark:	TECHNYL®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	dHwF8p_TECHNYLC52G2MV25GREYG1783CF.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Shin-Etsu Elastomer KE-9510U	Shin-Etsu Silicones of America	Silicone Rubber, HTV	Shin-Etsu Elastomer
TOTAL Polypropylene PPH 9020	TOTAL Refining & Chemicals	PP Homopolymer	TOTAL Polypropylene
APEX® 80-C118Q	Teknor Apex Company	PVC, Flexible	APEX®
Hysun® 678UV	Ravago Manufacturing Americas, LLC	ASA	Hysun®
Plaslube® HTN 05007	Techmer Engineered Solutions	Nylon, Unspecified	Plaslube®