Karina IVORY PVC COMPOUND 105800-35/ 1-B-ISE-LMP
| Category: | PVC, Unspecified , Polyvinyl Chloride |
| Manufacturer: | Karina Ind. e Com. de Plásticos Ltda |
| Trademark: | Karina |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dGzP65_Karina-IVORY-PVC-COMPOUND-105800-35-1-B-ISE-LMP.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| HEAVY METAL FREE PVC COMPOUND CLASS 105C (ST10) RECOMMENDED FOR JACKET OF ELECTRICAL CABLES. |
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.31 to 1.37 | g/cm³ | IEC 60811-1-3 |
| Cadmium Content | < 50 | ppm | IEC 62321 |
| Chromium Content | < 100 | ppm | IEC 62321 |
| Color | OK | ME 12 | |
| Color a | -1.69 to 1.31 | ME 12 | |
| Color b | 4.75 to 7.75 | ME 12 | |
| Color L | 88.2 to 91.2 | ME 12 | |
| Mercury Content | < 100 | ppm | IEC 62321 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Bromine Content | < 100 | ppm | IEC 62321 |
| Lead Content | < 100 | ppm | IEC 62321 |
| Maximum Variation of Elongation | < 25 | % | IEC 60811-1-2 |
| Maximum Variation of Tensile Strength | < 25 | % | IEC 60811-1-2 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 15 sec) | 78 to 82 | NBR 7456 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | > 13.7 | MPa | IEC 60811-1-1 |
| Tensile Strain (Yield) | > 200 | % | IEC 60811-1-1 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | > 13.7 | MPa | IEC 60811-1-2 |
| Tensile Elongation 3(Break) | > 200 | % | IEC 60811-1-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity 4 | > 1.0E+14 | ohms·cm | NBR 5403 |
| Note Message | |
|---|---|
| 1 . | 24 hr |
| 2 . | Aged in Air for 168 hr at 136°C |
| 3 . | Aged in Air for 168 hr at 136°C |
| 4 . | 24 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| 3M™ Dyneon™ Fluoroplastic FEP 6303Z | 3M Advanced Materials Division | FEP | 3M™ Dyneon™ Fluoroplastic |
| EXCELLOY CW10 | Techno Polymer Co, Ltd. | AES+PC | EXCELLOY |
| LUVOCOM® 1-8070 VP | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |
| PolyBlend™ 1100 55A | CardioTech International, Inc. | PUR, Unspecified | PolyBlend™ |
| Sylvin 9604-90 Clear Black 2103 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |