VENYL ST128 - 8689
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | AD majoris |
| Trademark: | VENYL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dGLg1P_VENYL-ST128---8689.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
VENYL ST128 - 8689 is a polyamide 6 with 15 % mineral, impact modified, black, intended for Injection moulding. APPLICATIONS VENYL ST128 - 8689 has been developed especially for very demanding applications in automotive industry and electrical parts. VENYL ST128 - 8689 is available in other colours, provided on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Molding Shrinkage | 0.80 to 1.2 | % | |
| Water Absorption (Equilibrium, 23°C, 50% RH) | 1.9 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3230 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 55.0 | MPa | ISO 527-2 |
| Flexural Modulus | 3100 | MPa | ISO 178 |
| Flexural Stress | 79.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 9.0 | kJ/m² | ISO 179 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 60.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | °C | ISO 3146 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+13 | ohms | DIN 53482 |
| Volume Resistivity | 1.0E+14 | ohms·cm | DIN 53482 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 265 to 280 | °C | |
| Middle Temperature | 255 to 270 | °C | |
| Front Temperature | 255 to 270 | °C | |
| Nozzle Temperature | 240 to 275 | °C | |
| Mold Temperature | 60.0 to 100 | °C | |
| Injection Pressure | 60.0 to 90.0 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 50.0 to 70.0 | MPa | |
| Screw L/D Ratio | 15.0:1.0 to 20.0:1.0 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| polyvic® E-1208-IL T | Unipack Plasindo | PVC, Flexible | polyvic® |
| Sup-tech S706 | Shanghai Suptech Engineering Plastics Co. Ltd. | ABS | Sup-tech |
| Zythane® 7090AF | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| Ateva® 2810A | Celanese EVA Performance Polymers | EVA | Ateva® |
| Sumiliteresin® PR-51732 | SBHPP | Phenolic | Sumiliteresin® |