OnForce™ LFT LF6600-5018 X2 NHFR NATURAL Datasheet,Nylon 66,PolyOne Corporation-SHANGHAI SUSHENG

Message
Polyvan's long fiber thermoplastic polymers are used in situations where high hardness and good impact resistance are required, such as metal substitution or other structural applications. These products exhibit enhanced physical and mechanical properties compared to staple fiber products. Its advantages include improved impact strength, elasticity and material strength in different temperature ranges. In addition, compared with traditional high-filled short fiber products, long fiber thermoplastic polymers show improved properties in terms of creep and fatigue resistance, improved dimensional stability and unique surface finish.

General Information
Filler / Reinforcement	Long glass fiber
Additive	Flame retardancy
Features	Thermal Stability Halogen-free
Forms	Particle

Physical	Nominal Value	Unit	Test Method
Density	1.59	g/cm³	ISO 1183
Molding Shrinkage ¹	0.20	%	ISO 294-4

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	15500	MPa	ISO 527-2
Tensile Stress (Break)	208	MPa	ISO 527-2
Tensile Strain (Break)	1.8	%	ISO 527-2
Flexural Modulus	11200	MPa	ISO 178
Flexural Stress	309	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	28	kJ/m²	ISO 179
Charpy Unnotched Impact Strength	80	kJ/m²	ISO 179
Dart Drop Impact	15.6	J	ASTM D5420

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
1.8 MPa, not annealed	240	°C	ISO 75-2/A
8.0 MPa, not annealed	210	°C	ISO 75-2/C

Electrical	Nominal Value	Unit	Test Method
Comparative Tracking Index	600	V	IEC 60112

Flammability	Nominal Value	Unit	Test Method
Flame Rating (1.60 mm)	V-0		UL 94
Glow Wire Flammability Index (1.60 mm)	960	°C	IEC 60695-2-12
Glow Wire Ignition Temperature (1.60 mm)	825	°C	IEC 60695-2-13
Oxygen Index	35	%	ISO 4589-2

Additional Information
Railway Applications-Fire Protection: Requirement/Hazard Level (EN 45545-2: 2013)Nominal Value: R22/HL2

Injection	Nominal Value	Unit
Drying Temperature	80.0	°C
Drying Time	4.0	hr
Processing (Melt) Temp	250 - 280	°C
Mold Temperature	90.0 - 120	°C
Injection Rate	Slow-Moderate
Back Pressure	2.50	MPa

Injection instructions
LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.It is recommended to purge the barrel as soon as the machine is standing still for a prolonged period of time to avoid the degradation of flame retardant fillers.

Injection instructions

LFT compounds can be processed using equipment similar to that used for short fiber products. The mechanical properties of finished parts depend greatly on the length of the fibers in the molded part; therefore processing conditions must be set carefully in order to minimize fiber breakage. A "low shear process" is advised, with low back pressure, low screw speed and low-to-medium injection speed.It is recommended to purge the barrel as soon as the machine is standing still for a prolonged period of time to avoid the degradation of flame retardant fillers.

Note Message
1 .	Measured on a tensile specimen. Actual mold shrinkage values are highly dependant on part geometry, mold configuration, and processing conditions.

Category:	Nylon 66 , Polyamide 66
Manufacturer:	PolyOne Corporation
Trademark:	OnForce™ LFT
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	dGFowg_OnForce-LFT-LF6600-5018-X2-NHFR-NATURAL.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
ColorRx® PE2-4000RX	LTL Color Compounders, Inc.	HDPE	ColorRx®
Grilamid® XE 4105 black 9992	EMS-GRIVORY	Nylon 610	Grilamid®
KOPLA PA6 KNP1000	KOPLA Co., Ltd.	Nylon 6	KOPLA PA6
Lucent PP GPP-230	Lucent Polymers, Inc.	PP, Unspecified	Lucent PP
Sylvin 3260-60 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin