Monprene® OM-10340 CLR
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Teknor Apex Company |
| Trademark: | Monprene® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dGA9wL_Monprene-OM-10340-CLR.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Monprene®OM-10340 CLR is a thermoplastic elastomer (TPE) material,. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is injection molding. Typical application areas include:
|
| General Information | |
|---|---|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.928 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 45 | g/10 min | ASTM D1238 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 45 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (300% Strain) | 2.93 | MPa | ASTM D412 |
| Tensile Strength (Break) | 6.89 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 750 | % | ASTM D412 |
| Additional Information | Nominal Value | ||
|---|---|---|---|
| Adhesion to ABS | |||
| Adhesion to HIPS | |||
| Adhesion to PS |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 65.6 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Rear Temperature | 188 - 238 | °C | |
| Middle Temperature | 193 - 238 | °C | |
| Front Temperature | 199 - 243 | °C | |
| Nozzle Temperature | 204 - 249 | °C | |
| Processing (Melt) Temp | 204 - 249 | °C | |
| Mold Temperature | 15.6 - 32.2 | °C | |
| Injection Pressure | 1.38 - 6.89 | MPa | |
| Injection Rate | Fast | ||
| Back Pressure | 0.172 - 0.862 | MPa | |
| Screw Speed | 50 - 120 | rpm | |
| Cushion | 3.81 - 25.4 | mm |
| Injection instructions |
|---|
| For any overmolding process it is recommended that the process temperatures for the TPE material be set at least 10 degrees Celsius higher than the melt temperature of the subtrate material. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Borealis PE FG5190 | Borealis AG | LLDPE | Borealis PE |
| Epoxies, Ect. 10-2080 HV | Epoxies, Etc. | PUR, Unspecified | Epoxies, Ect. |
| HiFill® PA6/6 CM16 HS BK | Techmer Engineered Solutions | Nylon 66 | HiFill® |
| ALTECH® PA6 A 4230/140 MR20 GF10 FR | ALBIS PLASTIC GmbH | Nylon 6 | ALTECH® PA6 |
| LNP™ STAT-KON™ RFD03 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ STAT-KON™ |