NORYL™ SE1X resin
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dG8sR1_NORYLSE1Xresin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PPO+PS. Improved productivity and reliability. Nonchlorinated, nonbrominated flame retardant. 244F HDT. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.10 | g/cm³ | ASTM D792 |
| Molding Shrinkage | Internal method | ||
| Flow : 3.20mm | 0.50 - 0.70 | % | Internal method |
| Transverse flow 1 | 0.50 - 0.70 | % | Internal method |
| Water Absorption (24 hr) | 0.060 | % | ASTM D570 |
| Outdoor Suitability | f1 | UL 746C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 2 | ASTM D638 | ||
| Yield | 67.6 | MPa | ASTM D638 |
| Fracture | 53.1 | MPa | ASTM D638 |
| Tensile Elongation 3 | ASTM D638 | ||
| Yield | 8.1 | % | ASTM D638 |
| Fracture | 20 | % | ASTM D638 |
| Flexural Modulus 4(100 mm Span) | 2500 | MPa | ASTM D790 |
| Flexural Strength 5(Yield, 100 mm Span) | 102 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 110 | J/m | ASTM D256 |
| 23°C | 210 | J/m | ASTM D256 |
| Instrumented Dart Impact | ASTM D3763 | ||
| -30°C, Energy at Peak Load | 32.5 | J | ASTM D3763 |
| 23°C, Energy at Peak Load | 51.5 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, unannealed, 6.40mm | 127 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 118 | °C | ASTM D648 |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 105 | °C | UL 746 |
| RTI | 110 | °C | UL 746 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | 2.3E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.20 mm, in Oil) | 18 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 50 Hz | 2.52 | ASTM D150 | |
| 60 Hz | 2.52 | ASTM D150 | |
| 1 MHz | 2.46 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 50 Hz | 3.4E-3 | ASTM D150 | |
| 60 Hz | 3.4E-3 | ASTM D150 | |
| 1 MHz | 2.1E-3 | ASTM D150 | |
| Arc Resistance 6 | PLC 6 | ASTM D495 | |
| Comparative Tracking Index (CTI) | PLC 1 | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) | PLC 4 | UL 746 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.47 mm | V-1 | UL 94 | |
| 5.99 mm | V-0 | UL 94 | |
| Radiant Panel Listing (UL) | RP100 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 104 - 110 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Suggested Shot Size | 30 - 70 | % | |
| Rear Temperature | 249 - 299 | °C | |
| Middle Temperature | 260 - 304 | °C | |
| Front Temperature | 271 - 310 | °C | |
| Nozzle Temperature | 282 - 310 | °C | |
| Processing (Melt) Temp | 282 - 310 | °C | |
| Mold Temperature | 76.7 - 104 | °C | |
| Back Pressure | 0.345 - 0.689 | MPa | |
| Screw Speed | 20 - 100 | rpm |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | 2.6 mm/min |
| 5 . | 2.6 mm/min |
| 6 . | Tungsten electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Mapex AN0920SN | Ginar Technology Co., LTD. | Nylon 6 | Mapex |
| BITONER® BT-1102 | Qingdao Bater Chemical Co., Ltd. | TP, Unspecified | BITONER® |
| DINAPLEN® PPH1S05 M403 H-4166 | Grupo Repol | PP Homopolymer | DINAPLEN® |
| KumhoSunny ABS HAG5230FR | Shanghai KumhoSunny Plastics Co., Ltd. | ABS | KumhoSunny ABS |
| Hypro-G™ PP-CP20 | Entec Polymers | PP Impact Copolymer | Hypro-G™ |