PRL TP-IG30
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Polymer Resources Ltd. |
| Trademark: | PRL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dF7ary_PRL-TP-IG30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
PRL TP-IG30 is a Polybutylene Terephthalate (PBT) product filled with 30% glass fiber. It can be processed by injection molding and is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (250°C/2.16 kg) | 5.0 to 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.40 to 0.80 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D638 | ||
| Yield, 3.18 mm | 110 | MPa | |
| Break, 3.18 mm | 110 | MPa | |
| Flexural Modulus (3.18 mm) | 6890 | MPa | ASTM D790 |
| Flexural Strength (Break, 3.18 mm) | 186 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.18 mm) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed, 3.18 mm | 213 | °C | |
| 1.8 MPa, Unannealed, 3.18 mm | 171 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 116 to 121 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 238 to 254 | °C | |
| Middle Temperature | 243 to 260 | °C | |
| Front Temperature | 249 to 266 | °C | |
| Processing (Melt) Temp | 232 to 260 | °C | |
| Mold Temperature | 71.1 to 87.8 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadraflex™ ARE-75A-B20 | Biomerics, LLC | TPU-Polyether | Quadraflex™ |
| TECHNYL® B 230 GREY 1429 H | Solvay Engineering Plastics | Nylon 66/6 | TECHNYL® B |
| ALCOM® PC 740/4 UV WT1201-08LD | ALBIS PLASTIC GmbH | PC | ALCOM® PC |
| Cheng Yu PE221 | Cheng Yu Plastic Company Limited | LDPE | Cheng Yu |
| LNP™ LUBRICOMP™ LCL36 compound | SABIC Innovative Plastics Europe | PEEK | LNP™ LUBRICOMP™ |