NORYL GTX™ GTX674PC resin
| Category: | PPE+PS+Nylon , Polyphenylene Ether + PS + Nylon |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | NORYL GTX™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dEGsvB_NORYL-GTX-GTX674PC-resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A conductive PPE/PA blend designed to have improved surface appearance and elevated heat resistance for powder coating. The material is suitable for injection molding. The material is only available in black. |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.11 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/5.0 kg) | 25 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 1.0 - 1.3 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1 | 2810 | MPa | ASTM D638 |
| Tensile Strength | |||
| Yield 2 | 65.0 | MPa | ASTM D638 |
| Fracture 3 | 64.0 | MPa | ASTM D638 |
| Fracture | 60.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Yield 4 | 3.0 | % | ASTM D638 |
| Yield | 3.0 | % | ISO 527-2/50 |
| Fracture 5 | 4.0 | % | ASTM D638 |
| Fracture | 4.0 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| 50.0mm span 6 | 2890 | MPa | ASTM D790 |
| -- 7 | 2480 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 103 | MPa | ISO 178 |
| Yield, 50.0mm span 8 | 109 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 50 | J/m | ASTM D256 |
| 23°C | 74 | J/m | ASTM D256 |
| Instrumented Dart Impact (23°C, Total Energy) | 4.00 | J | ASTM D3763 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 188 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 9 | 185 | °C | ISO 75-2/Bf |
| Vicat Softening Temperature | |||
| -- | 197 | °C | ASTM D1525, ISO 306/B50 9 10 |
| -- | 196 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | |||
| Flow : -40 to 40°C | 7.6E-5 | cm/cm/°C | ASTM E831 |
| Flow : 23 to 80°C | 8.1E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : -40 to 40°C | 7.8E-5 | cm/cm/°C | ASTM E831 |
| Lateral : 23 to 80°C | 8.6E-5 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+3 - 1.0E+4 | ohms·cm | Internal method |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 93.3 - 107 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Suggested Max Moisture | 0.070 | % | |
| Suggested Shot Size | 30 - 50 | % | |
| Rear Temperature | 266 - 304 | °C | |
| Middle Temperature | 271 - 304 | °C | |
| Front Temperature | 277 - 304 | °C | |
| Nozzle Temperature | 282 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 76.7 - 121 | °C | |
| Back Pressure | 0.345 - 1.38 | MPa | |
| Screw Speed | 20 - 100 | rpm | |
| Vent Depth | 0.013 - 0.038 | mm |
| Injection instructions |
|---|
| Minimum Moisture Content: 0.02 % |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type 1, 50mm/min |
| 3 . | Type 1, 50mm/min |
| 4 . | Type 1, 50mm/min |
| 5 . | Type 1, 50mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 mm |
| 10 . | 标准 B (120°C/h), 载荷2 (50N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sipolprene® 40171 | SIPOL S.p.A | TPC-ET | Sipolprene® |
| Chemical Resources BPP3500 | Chemical Resources, Inc. | PP Impact Copolymer | Chemical Resources |
| EnCom HH ABS 290 | EnCom, Inc. | ABS | EnCom |
| Hytrel® PC952 NC010 | DuPont Performance Polymers | TPC-ET | Hytrel® |
| LNP™ THERMOCOMP™ PF007S compound | SABIC Innovative Plastics | Nylon 6 | LNP™ THERMOCOMP™ |