Zytel® HTN 53G50HSLR BK083
| Category: | Nylon, Unspecified , HIGH PERFORMANCE POLYAMIDE RESIN |
| Manufacturer: | DuPont Performance Polymers |
| Trademark: | Zytel® HTN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dDGiar_Zytel-HTN-53G50HSLR-BK083.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 50% Glass Reinforced High Performance Polyamide with Improved Impact and Stiffness |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Part Marking Code (ISO 11469) |
|
| Part Marking Code (SAE J1344) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.59 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Across Flow | 0.50 | -- | % | |
| Flow | 0.20 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 16500 | 16500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 250 | 215 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 2.7 | 3.0 | % | ISO 527-2 |
| Tensile Creep Modulus | ISO 899-1 | |||
| 1 hr | -- | 10000 | MPa | |
| 1000 hr | -- | 7500 | MPa | |
| Flexural Modulus | 15300 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | |||
| -30°C | 13 | 13 | kJ/m² | |
| 23°C | 14 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 65 | 65 | kJ/m² | |
| 23°C | 95 | 90 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 100 | -- | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 254 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 234 | -- | °C | ISO 75-2/A |
| Melting Temperature 1 | 260 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow | 1.7E-5 | -- | cm/cm/°C | |
| Flow : -40 to 23°C | 1.9E-5 | -- | cm/cm/°C | |
| Transverse | 5.9E-5 | -- | cm/cm/°C | |
| Transverse : -40 to 23°C | 5.9E-5 | -- | cm/cm/°C | |
| Transverse : 55 to 160°C | 9.5E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Comparative Tracking Index | 550 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flammability Classification | IEC 60695-11-10, -20 | |||
| 0.750 mm | HB | -- | ||
| 1.50 mm | HB | -- | ||
| Oxygen Index | 27 | -- | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | First Heat |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Talcoprene® 520TL LE NERO | SO.F.TER. SPA | PP Homopolymer | Talcoprene® |
| Vyncolit® X6952 | Vyncolit N.V. | Phenolic | Vyncolit® |
| Baydur® 726 IBS (45 pcf) | Covestro - PUR | PUR-MDI | Baydur® |
| Laprene® 83FM00A65 | SO.F.TER. SPA | SEBS | Laprene® |
| LNP™ LUBRICOMP™ RAL22 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRICOMP™ |