Ebalta BLH Epoxy 200 / K 25
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Ebalta Kunststoff GmbH |
| Trademark: | Ebalta |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dBOpY6_Ebalta-BLH-Epoxy-200-K-25.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Slight discoleration of the hardener by oxygen possible. Discoleration to red-brown of hardener K 25 by oxygen, which doesn't affect the products quality. Demoulding of laminates made at room temperature (20°C) is possible. The parts show very good strength. To achieve maximum property values for example for flexural strength and heat resistance, we recommend thermal treatment at the recommended temperature. Applications
Properties
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Water Absorption | DIN 53495 | ||
| 23°C, 24 hr | 0.12 | % | |
| Saturation, 23°C 1 | 0.29 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D) | 78 to 82 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3250 to 3650 | MPa | ISO 527-2 |
| Tensile Stress | 80.0 to 86.0 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 5.1 to 5.5 | % | ISO 527-2 |
| Flexural Modulus | 2730 to 3080 | MPa | ISO 178 |
| Flexural Stress | 120 to 140 | MPa | ISO 178 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 79.0 to 83.0 | °C | ISO 75-2/A |
| Glass Transition Temperature | 85.0 | °C | TMA |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Hardener | Mix Ratio by Weight: 30 | ||
| Resin | Mix Ratio by Weight: 100 | ||
| Post Cure Time (80°C) | 12 to 15 | hr |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Density (20°C) | 1.11 to 1.15 | g/cm³ | |
| Viscosity (25°C) | 0.45 to 0.85 | Pa·s | |
| Curing Time (20°C) | 8.0 to 10 | hr | |
| Pot Life | |||
| 20°C 2 | 18 to 23 | min | |
| 20°C 3 | 20 to 25 | min |
| Note Message | |
|---|---|
| 1 . | 168 h |
| 2 . | 200 g |
| 3 . | 100 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TECHNYL® A 218C V10 NATURAL | Solvay Engineering Plastics | Nylon 66 | TECHNYL® A |
| Nanjing Hongrui PBT T1000 | Nanjing Hongrui Engineering Plastics Co., Ltd. | PBT | Nanjing Hongrui PBT |
| BMC 5436 | Bulk Molding Compounds, Inc. | Polyester, TS | BMC |
| EverGlide® MB5550P-WC | Polymer Dynamix | XLPE | EverGlide® |
| Hiprolon® 11 ESNNHL P20 | Arkema | Nylon 1012 | Hiprolon® |