EL-Pro™ P400S
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | SCG Chemicals Co., Ltd. |
| Trademark: | EL-Pro™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dB4OhU_EL-Pro-P400S.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| EL-Pro P400S is a homopolymer polypropylene resin which is suitable for monofilaments and flat yarn products. Which is manufacturered by extrusion process with spinnerette die, annular die, T-die, coathanger die, etc. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.5 | g/10 min | ASTM D1238 |
| Environmental Stress-Cracking Resistance (50°C, 25% Igepal, injection molding, F50) | > 500 | hr | ASTM D1693B |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 85 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength - Across Flow 1 | ASTM D638 | ||
| Yield | 31.4 | MPa | ASTM D638 |
| Fracture | 24.5 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 650 | % | ASTM D638 |
| Flexural Modulus | 1320 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -20°C | 17 | J/m | ASTM D256 |
| 0°C | 25 | J/m | ASTM D256 |
| 23°C | 39 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 60.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 155 | °C | ASTM D1525 |
| Melting Temperature | 163 | °C | ASTM D2117 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gloss | 65 | ASTM D2457 | |
| Haze | 50 | % | ASTM D1003 |
| Additional Information |
|---|
| Monofilament Processing -Melt temperature range: 250 to 280°CStretching Temperature: 95 to 110°CStretching Ratio: 8 to 12Flat yarn Processing -Melt temperature range: 220 to 270°CStretching Temperature: 120 to 140°CStretching Ratio: 5 to 7 |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2900-50 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Wah Hong DAP WH-9100- BLK HM | Wah Hong Industrial Corp. | DAP | Wah Hong DAP |
| WELLAMID Nylon 6000 GV 25 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |
| LNP™ THERMOCOMP™ EC006APQ compound | SABIC Innovative Plastics | PEI | LNP™ THERMOCOMP™ |
| Polimid B 40 | Poliblend S.p.a. | Nylon 6 | Polimid B |