PLUSTEK RB306G6
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Polyram Ram-On Industries |
| Trademark: | PLUSTEK |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | dA3uR6_PLUSTEK-RB306G6.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 30% GLASS-FIBER REINFORCED, HEAT STABILIZED POLYAMIDE 6 FOR INJECTION MOULDING APPLICATIONS. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.35 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| Saturation | 6.6 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 2.1 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 122 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 140 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 7000 | MPa | ASTM D790 |
| Flexural Strength | 200 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 80 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 217 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 205 | °C | ASTM D648 |
| Maximum operating temperature- Short Peaks Operation | 200 | °C | |
| Maximum Continuous Use Temperature | 110 | °C | |
| Peak Melting Temperature | 218 | °C | ASTM D3418 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (3.00 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 85.0 | °C | |
| Drying Time | 3.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Rear Temperature | 220 - 260 | °C | |
| Middle Temperature | 230 - 265 | °C | |
| Front Temperature | 250 - 270 | °C | |
| Mold Temperature | 55.0 - 95.0 | °C | |
| Injection Pressure | 70.0 - 105 | MPa | |
| Injection Rate | Fast | ||
| Holding Pressure | 30.0 - 70.0 | MPa | |
| Back Pressure | 0.350 - 0.700 | MPa | |
| Screw Speed | 60 - 90 | rpm |
| Injection instructions |
|---|
| Fill Speed: 50 to 75 mm/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Fainplast PVC MPH 62/T | Fainplast Compounds S.r.l | PVC, Flexible | Fainplast PVC |
| Geon™ Vinyl Rigid Molding M3400 | PolyOne Corporation | PVC, Rigid | Geon™ Vinyl Rigid Molding |
| Huafon JF-PDY-P531H | Huafon Group Co., Ltd. | PUR, Unspecified | Huafon |
| LUVOCOM® 1106-8232 | Lehmann & Voss & Co. | PEI | LUVOCOM® |
| Sylvin 2808-80 White 1440 | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |