LNP™ THERMOCOMP™ D452 compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics Asia Pacific |
| Trademark: | LNP™ THERMOCOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d9kfPP_LNP-THERMOCOMP-D452-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* Thermocomp* D452 (or EXTC8202) is a compound based on SABIC unique Polycarbonate copolymer resin containing Glass Fiber, Flame Retardant. Added features of this material include: High modulus, good flatness, good ductility, Non-Brominated & Non-Chlor |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.52 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) | ASTM D1238 | ||
| 300°C/1.2 kg | 17 | g/10 min | |
| 300°C/2.16 kg | 39 | g/10 min | |
| Melt Volume-Flow Rate (MVR) | ISO 1133 | ||
| 300°C/1.2 kg | 12.0 | cm³/10min | |
| 300°C/2.16 kg | 30.0 | cm³/10min | |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 0.10 to 0.25 | % | |
| Across Flow : 24 hr | 0.10 to 0.25 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 12000 | MPa | ASTM D638 |
| -- | 11300 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 141 | MPa | ASTM D638 |
| Break | 140 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Break 3 | 2.3 | % | ASTM D638 |
| Break | 2.2 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 4 | 11700 | MPa | ASTM D790 |
| -- 5 | 10100 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 189 | MPa | ISO 178 |
| Break, 50.0 mm Span 6 | 211 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 7(23°C) | 13 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength 8(23°C) | 41 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact (23°C) | 150 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C) | 620 | J/m | ASTM D4812 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 98.0 | °C | ASTM D648 |
| CLTE | ISO 11359-2 | ||
| Flow : 23 to 80°C | 1.6E-5 | cm/cm/°C | |
| Transverse : 23 to 80°C | 5.8E-5 | cm/cm/°C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.00 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 to 100 | °C | |
| Drying Time | 3.0 to 5.0 | hr | |
| Rear Temperature | 265 to 280 | °C | |
| Middle Temperature | 270 to 310 | °C | |
| Front Temperature | 275 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 70.0 to 110 | °C | |
| Back Pressure | 0.300 to 1.00 | MPa | |
| Screw Speed | 20 to 100 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | 1.3 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 80*10*4 sp=62mm |
| 8 . | 80*10*4 sp=62mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SABIC® LDPE 2404H4 | Saudi Basic Industries Corporation (SABIC) | LDPE | SABIC® LDPE |
| Michimid K4200GF13-03 | API Polymers, Inc. | Nylon 66 | Michimid |
| Shin-Etsu Elastomer KE-5550U | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| ENVIROSUN® ENV31-NC070 | ENVIROPLAS®, Inc. | ASA | ENVIROSUN® |
| Karina GRAY PVC COMPOUND 950-18/277-C-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |