EPO-TEK® 383ND
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d97l50_EPO-TEK-383ND.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| A slightly longer pot life version of EPO-TEK®353ND designed for high temperature, optical and structural applications inside the semiconductor, hybrid, electronic, fiber optic and medical industries. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 415 | °C | |
| Die Shear Strength - >20 kg (23°C) | 46.9 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 250 | °C | |
| Intermittent | -55 to 350 | °C | |
| Storage Modulus | 2.54 | GPa | |
| Weight Loss on Heating | |||
| 200°C | 0.28 | % | |
| 250°C | 0.42 | % | |
| 300°C | 0.86 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | > 100 | °C | |
| CLTE - Flow | |||
| -- 2 | 3.4E-5 | cm/cm/°C | |
| -- 3 | 1.3E-4 | cm/cm/°C |
| Optical | Nominal Value | Unit | |
|---|---|---|---|
| Refractive Index 4 | 1.572 | ||
| Transmittance (520 to 1660 nm) | > 90.0 | % |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.0 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 5 | Clear/Transparent | ||
| -- 6 | Yellow | ||
| Density | |||
| Part B | 0.988 | g/cm³ | |
| Part A | 1.20 | g/cm³ | |
| Viscosity 7(23°C) | 3.5 to 6.0 | Pa·s | |
| Curing Time (150°C) | 1.0 | hr | |
| Pot Life | 480 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore D) | 88 | ||
| Lap Shear Strength (23°C) | > 13.8 | MPa | |
| Relative Permittivity (1 kHz) | 2.58 | ||
| Volume Resistivity (23°C) | > 3.0E+13 | ohms·cm | |
| Dissipation Factor (1 kHz) | 8.0E-3 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | 589 nm |
| 5 . | Part A |
| 6 . | Part B |
| 7 . | 50 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® D6870 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| Polypropylene PP 10 CA | PETKIM Petrokimya Holding A.S. | PP, Unspecified | Polypropylene |
| Selvol™ 310 | Sekisui Chemical Company, Ltd. | PVOH | Selvol™ |
| Kepital® TE-24(FU2020) | KEP Americas | Acetal (POM) Copolymer | Kepital® |
| PIVINEL™ KAZ-32 | HELLENIC CABLES S.A. | PVC, Unspecified | PIVINEL™ |