| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Vamp Tech |
| Trademark: | DELOXEN |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d8QK5p_DELOXEN-2010.pdf |
| PRICE: | Order Products email sales@su-jiao.com |
| Message |
|---|
| PPO, 20% glass fiber reinforced, not Flame Retardant compound, good mechanical properties. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | ||
| Flow | 0.20 | % | |
| Across Flow | 0.30 | % | |
| Water Absorption (Saturation) | 0.20 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 6000 | MPa | ASTM D638 |
| Tensile Strength (Yield) | 70.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.8 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength | 6.5 | kJ/m² | ISO 180/A |
| Unnotched Izod Impact Strength | 25 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 120 | °C | ASTM D648A |
| Vicat Softening Temperature | 135 | °C | ASTM D1525 1 |
| RTI Elec | 110 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI Str | 110 | °C | UL 746 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 290 | °C | |
| Mold Temperature | 90.0 | °C |
| Note Message | |
|---|---|
| 1 . | Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SkinFlex III Brushable | BJB Enterprises, Inc. | TSU | SkinFlex III |
| Forprene® 6NE001A80 | SO.F.TER. SPA | TPV | Forprene® |
| Golden Compound PP S²PC 3545 BO 10IM16 | Golden Compound GmbH | PP, Unspecified | Golden Compound |
| Karina BLACK PVC COMPOUND 105751-48/ 1-B-AC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ THERMOCOMP™ MB006HS compound | SABIC Innovative Plastics | PP, Unspecified | LNP™ THERMOCOMP™ |