Durepol® PBT A3 G15 TZ NTLA010 BT327
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Petropol Industry and Trade of Polymers LTDA |
| Trademark: | Durepol® PBT |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d8G6rB_Durepol-PBT-A3-G15-TZ-NTLA010-BT327.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PBT polyester natural reinforced with 15% of fiberglass and impact modified, good set of thermal and mechanical properties. Ideal for injection molding. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.37 | g/cm³ | ASTM D792 |
| Melt Volume-Flow Rate (MVR) (260°C/2.16 kg) | 15.0 | cm³/10min | ASTM D1238 |
| Water Absorption (Equilibrium) | 0.30 | % | ASTM D570 |
| Ash Content | 13 to 17 | % | ASTM D2584 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 5200 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 92.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 38 | % | ASTM D638 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C | 60 | J/m | |
| 23°C | 110 | J/m | |
| Unnotched Izod Impact | ASTM D256 | ||
| -30°C | 330 | J/m | |
| 23°C | 610 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 217 | °C | |
| 1.8 MPa, Unannealed | 197 | °C | |
| Vicat Softening Temperature | 219 | °C | ASTM D1525 |
| Melting Temperature 1 | 224 | °C | ASTM D2117 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Volume Resistivity | > 1.0E+13 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 | °C | |
| Drying Time | 6.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Processing (Melt) Temp | 250 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SLOVAMID® 6 T 15 | Plastcom | Nylon 6 | SLOVAMID® 6 |
| Moplen EPC30M | Shazand (Arak) Petrochemical Corporation | PP Copolymer | Moplen |
| Nordbak Cold Cure Backing | Loctite® | Epoxy | Nordbak |
| Gravi-Tech™ GRV-NY-035-SS-GF-BLK | PolyOne Corporation | Nylon 6 | Gravi-Tech™ |
| Wankai WK821 | Zhejiang Wankai New Materials Co., Ltd. | PET | Wankai |