Infino XI-2008F
| Category: | PPS+PPA , Polyphenylene Sulfide + PPA |
| Manufacturer: | SAMSUNG SDI CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d7uy9l_Infino-XI-2008F.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino XI-2008F is a Polyphenylene Sulfide + PPA (PPS+PPA) product filled with mineral. It is available in Africa & Middle East, Asia Pacific, Europe, Latin America, or North America. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.20 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 10 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 109 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | |||
| Yield 1 | 29.0 | MPa | ASTM D638 |
| Yield | 30.0 | MPa | ISO 527-2/5 |
| Flexural Modulus 2 | |||
| -- | 11000 | MPa | ASTM D790 |
| -- | 9000 | MPa | ISO 178 |
| Flexural Strength 3 | |||
| -- | 59.0 | MPa | ASTM D790 |
| -- | 60.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 4(23°C) | 3.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C, 3.18 mm | 20 | J/m | ASTM D256 |
| 23°C 5 | 3.5 | kJ/m² | ISO 180/1A |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 120 | °C | |
| Desiccant Dryer | 120 | °C | |
| Drying Time | |||
| -- | 4.0 to 6.0 | hr | |
| Desiccant Dryer | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | < 0.050 | % | |
| Rear Temperature | 280 to 290 | °C | |
| Middle Temperature | 290 to 300 | °C | |
| Front Temperature | 310 to 320 | °C | |
| Nozzle Temperature | 320 | °C | |
| Mold Temperature | 120 to 140 | °C | |
| Injection Pressure | 49.0 to 127 | MPa | |
| Back Pressure | 0.490 to 1.96 | MPa | |
| Screw Speed | 50 to 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 2.8 mm/min |
| 3 . | 2.8 mm/min |
| 4 . | Thickness: 4 mm |
| 5 . | Thickness: 4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| EVICOM™ RC7/025 | INEOS Compounds | PVC, Rigid | EVICOM™ |
| EZ-Brush® Vacuum Bagging Silicone | Smooth-On, Inc | Silicone | EZ-Brush® |
| Huafon T23H | Huafon Group Co., Ltd. | Nylon 66 | Huafon |
| LNP™ THERMOCOMP™ NX10302 compound | SABIC Innovative Plastics Asia Pacific | PC+ABS | LNP™ THERMOCOMP™ |
| Sylvin 3270-85 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |