U-polymer AXF-1500-05
| Category: | Polyarylate , Polyarylate |
| Manufacturer: | UNITIKA Plastics Division |
| Trademark: | U-polymer |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d7dIMh_U-polymer-AXF-1500-05.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AX Series Resins Composite Grade |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Forms |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.19 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (3.00 mm) | 1.0 | -- | % | ASTM D955 |
| Water Absorption (24 hr, 3.18 mm) | 0.75 | -- | % | ASTM D570 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale) | 105 | -- | ASTM D785 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Strength | 67.0 | 54.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 15 | 22 | % | ASTM D638 |
| Flexural Modulus | 2600 | 1100 | MPa | ASTM D790 |
| Flexural Strength | 100 | 78.0 | MPa | ASTM D790 |
| Compressive Strength | 82.0 | -- | MPa | ASTM D695 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (3.18 mm) | 54 | 150 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 150 | -- | °C | ASTM D648 |
| CLTE - Flow | 7.4E-5 | -- | cm/cm/°C | ASTM D696 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | -- | 1.0E+14 | ohms·cm | ASTM D257 |
| Dielectric Strength | -- | 25 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | -- | 3.60 | ASTM D150 | |
| Dissipation Factor (1 MHz) | -- | 0.040 | ASTM D150 | |
| Arc Resistance | -- | 80.0 | sec | ASTM D495 |
| Additional Information |
|---|
| 干燥 Limiting PV Value: 424 kPa - m/sCoefficient of Dynamic Coefficient: 0.15 to 0.2 |
| 调节后的 Limiting PV Value: 424 kPa - m/sCoefficient of Dynamic Coefficient: 0.15 to 0.2 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MAXAMID™ PA66G50 | Pier One Polymers, Inc. | Nylon 66 | MAXAMID™ |
| Toyolac® 100 X01 | Toray Plastics (Malaysia) Sdn. Bhd. | ABS | Toyolac® |
| Beetle® PET100 | Teknor Apex Company (Chem Polymer) | PET | Beetle® |
| Fainplast PVC GSO 70/33 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| POCAN® TP 306-201 000000 | LANXESS GmbH | PBT+ASA | POCAN® |