RELENE® F18020
| Category: | LLDPE , Linear Low Density Polyethylene |
| Manufacturer: | Reliance Industries Limited |
| Trademark: | RELENE® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d7MbIi_RELENE-F18020.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| F18020 is a butene comonomer based Linear Low Density Polyethylene (LLDPE), with optimum levels of antioxidants and polymer processing aid, but without antiblock and without slip additives. The grade is designed for manufacturing cast films, air bubble films and films for lamination applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.917 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 2.0 | g/10 min | ASTM D1238 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 40 µm, Blown Film | 12.5 | MPa | |
| TD : Yield, 40 µm, Blown Film | 12.0 | MPa | |
| MD : Break, 40 µm, Blown Film | 30.0 | MPa | |
| TD : Break, 40 µm, Blown Film | 25.0 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 40 µm, Blown Film | 700 | % | |
| TD : Break, 40 µm, Blown Film | 800 | % | |
| Dart Drop Impact (40 µm, Blown Film) | 120 | g | ASTM D1709A |
| Elmendorf Tear Strength | ASTM D1922 | ||
| MD : 40 µm, Blown Film | 80 | g | |
| TD : 40 µm, Blown Film | 290 | g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S BMV150K 333 NER 2578 | Radici Plastics | Nylon 6 | Radilon® |
| RheTech Polypropylene RCC233-01 | RheTech, Inc. | PP Copolymer | RheTech Polypropylene |
| Nylene® 724 HS | Custom Resins Group | Nylon 6 | Nylene® |
| Cellidor CP 310-10 | ALBIS PLASTIC GmbH | CAP | Cellidor |
| POLYfill PP CQX10030 R3 | Polykemi AB | PP, Unspecified | POLYfill |