Badamid® B70
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | Bada AG |
| Trademark: | Badamid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d7HKD5_Badamid-B70.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Low viscosity standard injection moulding grade for thin walled applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.13 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 9.5 | -- | % | |
| Equilibrium, 23°C, 50% RH | 3.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3100 | 1300 | MPa | ISO 527-2/1 |
| Tensile Stress 1(Yield, 23°C) | 85.0 | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain 2(Yield, 23°C) | 4.5 | 20 | % | ISO 527-2/50 |
| Nominal Tensile Strain at Break 3(23°C) | 15 | > 50 | % | ISO 527-2/50 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength 4 | ISO 179/1eA | |||
| -30°C | 7.0 | 8.0 | kJ/m² | |
| 23°C | 8.0 | 60 | kJ/m² | |
| Charpy Unnotched Impact Strength 5 | ISO 179/1eU | |||
| -30°C | No Break | No Break | ||
| 23°C | No Break | No Break | ||
| Notched Izod Impact Strength 6 | ISO 180/1A | |||
| -30°C | 5.0 | -- | kJ/m² | |
| 23°C | 7.0 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 7 | ||||
| 0.45 MPa, Unannealed | 175 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 65.0 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) 8 | 222 | -- | °C | ISO 3146 |
| CLTE - Flow 9(4.00 mm) | 8.5E-5 | -- | cm/cm/°C | DIN 53752 |
| Maximum Service Temperature | IEC 216 | |||
| 20000 hrs | 70 | -- | °C | |
| some hours | 170 | -- | °C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity 10 | 1.0E+13 | 1.0E+10 | ohms | IEC 60093 |
| Volume Resistivity 11 | 1.0E+15 | 1.0E+12 | ohms·cm | IEC 60093 |
| Electric Strength 12 | 100 | 60 | kV/mm | IEC 60243-1 |
| Relative Permittivity 13(1 MHz) | 3.40 | 7.00 | IEC 60250 | |
| Dissipation Factor 14(1 MHz) | 0.023 | 0.30 | IEC 60250 | |
| Comparative Tracking Index | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating | UL 94 | |||
| 0.800 mm 15 | V-2 | -- | ||
| 1.60 mm 16 | V-2 | -- |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | Test Specimen accordng to ISO 3167, Type A |
| 4 . | 80x10x4 mm |
| 5 . | 80x10x4 mm |
| 6 . | 80x10x4 mm |
| 7 . | 110x10x4mm |
| 8 . | 10 K/min, Compound for moulding |
| 9 . | >=10x10x4 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 80x80x1 mm |
| 13 . | 80x80x1 mm |
| 14 . | 80x80x1 mm |
| 15 . | 125x13x0.8 mm |
| 16 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCANBLEND P AP2060 F30B | Polykemi AB | PBT+ASA | SCANBLEND P |
| Silamid® G10 | Roonamid a.s. | Nylon 6 | Silamid® |
| Nanguang TPU S-72DX | Fujian Nanguang Light Industry Co., Ltd. | TPU, Unspecified | Nanguang TPU |
| Nylene® 494 | Custom Resins Group | Nylon 6 | Nylene® |
| OmniCarb™ PC08FR510 | OMNI Plastics, LLC | PC | OmniCarb™ |