Rilsan® CLEAR G 170
| Category: | Nylon 11 , Polyamide 11 |
| Manufacturer: | Arkema |
| Trademark: | Rilsan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d6RP45_Rilsan-CLEAR-G-170.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Rilsan ® Clear G 170 is a high performance transparent polyamide with outstanding thermal resistance. This grade has been designed for extrusion and injection molding applications. MAIN APPLICATIONS
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Molding Shrinkage | Internal Method | ||
| Across Flow : 40°C, 24 hr, 2.00 mm | 0.72 | % | |
| Flow : 40°C, 24 hr, 2.00 mm | 0.69 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 3.8 | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness | ISO 868 | ||
| Shore D | 84 | ||
| Shore D, 15 sec | 79 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2020 | MPa | ISO 527-2 |
| Tensile Stress | ISO 527-2 | ||
| Yield | 74.0 | MPa | |
| Break | 58.0 | MPa | |
| Tensile Strain | ISO 527-2 | ||
| Yield | 9.0 | % | |
| Break | > 100 | % | |
| Flexural Modulus | 1980 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 13 | kJ/m² | |
| 23°C | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 150 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 136 | °C | ISO 75-2/A |
| Glass Transition Temperature | 168 | °C | ISO 11357-2 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (2000 µm, 560 nm) | 90.8 | % | ASTM D1003 |
| Refractive Index | 1.5380 | ISO 489 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Processing (Melt) Temp | 270 to 310 | °C | |
| Mold Temperature | 40.0 to 80.0 | °C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Melt Temperature | 270 to 290 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Bergamid™ PA66 C20 Black | PolyOne Corporation | Nylon 66 | Bergamid™ |
| Fenochem R 4700 | Chemiplastica, Inc. | Phenolic | Fenochem |
| Elastollan® 1185A10 | BASF Corp. Thermoplastic Polyurethanes | TPU-Polyether | Elastollan® |
| Elastocon® OF65 | Elastocon TPE Technologies | TPE | Elastocon® |
| LNP™ LUBRILOY™ R2000 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ LUBRILOY™ |