Boda BDT2461I
| Category: | Fluorelastomer , Fluoroelastomer |
| Manufacturer: | Chenguang Fluoro & Silicone Elastomers Co., Ltd. |
| Trademark: | Boda |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d6QZy6_Boda-BDT2461I.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
BDT2461I is a low viscosity curative incorporated fluoroelastomer terpolymer. This grade is well suited for application where good flowability and superior fluid resistance than copolymers are required. BDT2461I can be compounded to meet the major fluoroelastomer specifications. BDT2461I can be used for injection and transfer molding, and extrusion of O-rings and gaskets. It can be mixed using typical fluoroelastomer compounding ingredients. Mixing can be accomplished with two-roll mills or internal mixers. Finished goods can be produced by a variety of rubber processing methods. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.86 | g/cm³ | |
| Mooney Viscosity (ML 1+10, 121°C) | 26 | MU | |
| Fluorine Content | 68 | % | |
| Solubility | LMW Ketones and esters |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| MH 1(177°C) | 2.27 | N·m | |
| ML 2(177°C) | 0.200 | N·m | |
| t'90 3(177°C) | 2.6 | min | |
| ts2 4(177°C) | 55.0 | sec |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness 5(Shore A) | 79 | ASTM D2240 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 6(Yield) | 12.0 | MPa | ASTM D412 |
| Tensile Elongation 7(Break) | 230 | % | ASTM D412 |
| Compression Set (200°C, 70 hr) | 26 | % | ASTM D395B |
| Additional Information |
|---|
| Test Compound: Polymer: 100 MT Black (N990): 30 phr MgO: 3 phr Ca(OH)2: 6 phr Curing Condition: Press: 10 min at 170°C Oven: 24 hr at 230°C |
| Note Message | |
|---|---|
| 1 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 2 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 3 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 4 . | MDR2000 Rheometer, 100cpm, 0.5° Arc, 6 minutes |
| 5 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 6 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| 7 . | Press Time: 10 min, Press Temperature: 170°C, Post Cure Time: 24 hr, Post Cure Temperature: 230°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Nypol® PA B3 G30 LRJ0319 NT368 | Petropol Industry and Trade of Polymers LTDA | Nylon 6 | Nypol® PA |
| AIE PC 1010F-T6 | Asia International Enterprise (Hong Kong) Limited | PC | AIE PC |
| Eporex® HIPS 830 | Eternal Plastics Co., Ltd. | PS (HIPS) | Eporex® |
| Karina WHITE PVC COMPOUND 924D10/349-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Axiall PVC 7255 | Axiall Corporation | PVC, Rigid | Axiall PVC |