LNP™ LUBRICOMP™ IAL12 compound
| Category: | Nylon 612 , Polyamide 612 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d6Gtw3_LNP-LUBRICOMP-IAL12-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP* LUBRICOMP* IAL12 is a compound based on Nylon 6/12 resin containing 5% PTFE, 10% Aramid Fiber. Added feature of this material is: Wear Resistant. Also known as: LNP* LUBRICOMP* Compound IAL-4012 Product reorder name: IAL12 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.13 | g/cm³ | ASTM D792 |
| -- | 1.12 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ASTM D955 | ||
| Flow : 24 hr | 1.0 to 3.0 | % | |
| Across Flow : 24 hr | 2.0 to 4.0 | % | |
| Water Absorption | |||
| 24 hr, 50% RH | 0.21 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.32 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 3170 | MPa | ASTM D638 |
| -- | 2920 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Break 2 | 65.0 | MPa | ASTM D638 |
| Break | 63.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 3 | 8.1 | % | ASTM D638 |
| Yield | 8.2 | % | ISO 527-2/5 |
| Break 4 | 8.6 | % | ASTM D638 |
| Break | 8.8 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 5 | 2840 | MPa | ASTM D790 |
| -- 6 | 2630 | MPa | ISO 178 |
| Flexural Stress | 74.0 | MPa | ISO 178 |
| Coefficient of Friction | ASTM D3702 Modified | ||
| vs. Itself - Dynamic | 0.46 | ||
| vs. Itself - Static | 0.41 | ||
| Wear Factor | ASTM D3702 Modified | ||
| Ring | 0.0500 | 10^-10 in^5-min/ft-lb-hr | |
| Washer | 31.0 | 10^-10 in^5-min/ft-lb-hr |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 7 | 2.2 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 490 | J/m | ASTM D4812 |
| 23°C 8 | 39 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Total Energy | 4.20 | J | ASTM D3763 |
| -- | 1.10 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 187 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 9 | 172 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 92.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 10 | 90.0 | °C | ISO 75-2/Af |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.12 to 0.20 | % | |
| Rear Temperature | 254 to 266 | °C | |
| Middle Temperature | 260 to 271 | °C | |
| Front Temperature | 271 to 282 | °C | |
| Processing (Melt) Temp | 271 to 277 | °C | |
| Mold Temperature | 65.6 to 93.3 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | 1.3 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 80*10*4 mm |
| 10 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Rhelon M1020H-01 | RheTech, Inc. | Nylon 6 | Rhelon |
| Starflam AFR430B1 | Eurostar Engineering Plastics | Nylon 66 | Starflam |
| Alcryn® 4080 NC | Advanced Polymer Alloys | MPR | Alcryn® |
| Fiberfil® J-69/40/E | Fiberfil® Engineered Plastics Inc. | PP Homopolymer | Fiberfil® |
| EnCom F0 GF10 PC | EnCom, Inc. | PC | EnCom |