Lupoy® GN1006FT
| Category: | PC , Polycarbonate |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Lupoy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d5l1Na_Lupoy-GN1006FT.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Lupoy® GN1006FT is a Polycarbonate (PC) material. It is available in Asia Pacific, Europe, Latin America, or North America for injection molding. Important attributes of Lupoy® GN1006FT are:
Typical application of Lupoy® GN1006FT: Electrical/Electronic Applications |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 30 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.20 mm) | 0.50 to 0.80 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Yield, 3.20 mm) | 61.8 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 3.20 mm) | > 100 | % | ASTM D638 |
| Flexural Modulus 3(3.20 mm) | 2260 | MPa | ASTM D790 |
| Flexural Strength 4(3.20 mm) | 91.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 6.40 mm) | 130 | °C | ASTM D648 |
| RTI Elec | 120 | °C | UL 746 |
| RTI Imp | 110 | °C | UL 746 |
| RTI Str | 120 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 2.00 mm | V-1 | ||
| 2.50 mm | V-0 | ||
| 3.00 mm | V-0 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance | 89.0 | % | ASTM D1003 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 to 115 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 240 to 260 | °C | |
| Middle Temperature | 255 to 275 | °C | |
| Front Temperature | 270 to 285 | °C | |
| Nozzle Temperature | 270 to 285 | °C | |
| Processing (Melt) Temp | 255 to 285 | °C | |
| Mold Temperature | 50.0 to 80.0 | °C | |
| Back Pressure | 0.981 to 3.92 | MPa | |
| Screw Speed | 40 to 70 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 10 mm/min |
| 4 . | 10 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Shandong PA610 A6G7301 | Shandong Dongchen Engineering Plastics Co., Ltd. | Nylon 610 | Shandong PA610 |
| ARC ARC1420 | ARC Resin Corporation | ABS | ARC |
| Hanwha Total PP HY311 | HANWHA TOTAL PETROCHEMICALS Co., Ltd. | PP Homopolymer | Hanwha Total PP |
| Karina BLACK COLOR CONCENTRATE 48/1-GI (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1850/GF/30/TF/13/SI/2/BK | Lehmann & Voss & Co. | PBT | LUVOCOM® |