EMERGE™ PC 4330ECO
| Category: | PC , Advanced Resin |
| Manufacturer: | Trinseo |
| Trademark: | EMERGE™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d5Wfa5_EMERGE-PC-4330ECO.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EMERGE PC 4330ECO Advanced Polycarbonate Resin contains 50% post consumer recycled (PCR) polycarbonate with IEEE 1680:2006 certified by TÜV Rheinland. Its color under the code of IC8800234 meets the stringent requirement of white. This resin also provides a property balance of flowability, ductility, stiffness and thermal resistance to meet the market needs on various applications in information technology equipment (ITE) and consumer electronics without painting or coating. Applications
|
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.26 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 23 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness | ASTM D2240 | ||
| Shore A, 3.20 mm, Injection Molded | 99 | ||
| Shore D, 3.20 mm, Injection Molded | 86 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2200 | MPa | ASTM D638 |
| Tensile Strength (Yield, 3.20 mm, Injection Molded) | 62.0 | MPa | ASTM D638 |
| Tensile Elongation (Break, 3.20 mm, Injection Molded) | 110 | % | ASTM D638 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2450 | MPa | ASTM D790 |
| Flexural Strength (3.20 mm, Injection Molded) | 96.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 131 | °C | |
| 1.8 MPa, Unannealed | 119 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 60.0 to 90.0 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sinvicomp SGH2500 | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Sinvicomp |
| EXCELLOY SXJ220 | Techno Polymer Co, Ltd. | ABS | EXCELLOY |
| HANWHA CLBA-8450BK | Hanwha Chemical | LLDPE | HANWHA |
| TABOREN® PH 41 G 30-095 | SILON s.r.o. | PP Homopolymer | TABOREN® |
| FUDOWPREMIX® FP100F typeA | Fudow Co., Ltd. | Polyester, TS | FUDOWPREMIX® |