Sumitomo Silicone SI 9002N-1
| Category: | Silicone , Silicone |
| Manufacturer: | Sumitomo Bakelite North America, Inc. |
| Trademark: | Sumitomo Silicone |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d3vRnQ_Sumitomo-Silicone-SI-9002N-1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| SI 9002N-1 is a short fiberglass reinforced silicone molding compound, which offers moderate strength properties, and dimensional stability and excellent long-term thermal stability at elevated temperatures. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 2.10 | g/cm³ | ASTM D792 |
| Apparent Density | 0.90 | g/cm³ | ASTM D1895 |
| Molding Shrinkage - Flow | 0.20 to 0.40 | % | ASTM D955 |
| Water Absorption - 48 hr (50°C) | 0.30 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale, Compression Molded) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break, Compression Molded) | 27.0 | MPa | ASTM D638 |
| Flexural Modulus (Compression Molded) | 14000 | MPa | ASTM D790 |
| Flexural Strength (Break) | 52.0 | MPa | ASTM D790 |
| Compressive Strength | 88.0 | MPa | ASTM D695 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (Compression Molded) | 22 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, Compression Molded) | > 282 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength 1 | ASTM D149 | ||
| -- 2 | 9.8 | kV/mm | |
| -- 3 | 6.5 | kV/mm | |
| Dielectric Constant 4(1 MHz) | 3.90 | ASTM D2520 | |
| Dissipation Factor 5(1 MHz) | 0.020 | ASTM D150 | |
| Arc Resistance | 200 | sec | ASTM D495 |
| Note Message | |
|---|---|
| 1 . | Wet, 60 Hz |
| 2 . | Method A (Short-Time) |
| 3 . | Method B (Step-by-Step) |
| 4 . | Wet |
| 5 . | Wet |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Vi-Chem PVC VNC110E | Vi-Chem Corporation | PVC, Rigid | Vi-Chem PVC |
| Topolymer® 5321-951E | Dongguan Top Polymer Enterprise | TPE | Topolymer® |
| Durepol® PBT A3 V20 CNZ0350 BT331 | Petropol Industry and Trade of Polymers LTDA | PBT | Durepol® PBT |
| Epoxies, Ect. 10-3216 Gray | Epoxies, Etc. | Epoxy | Epoxies, Ect. |
| OP - PBT 25GB-5GF-IM | Oxford Polymers | PBT | OP - PBT |