Latilon 28D G/30
| Category: | PC , Polycarbonate |
| Manufacturer: | LATI S.p.A. |
| Trademark: | Latilon |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d3WL9E_Latilon-28D-G-30.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Compound based on Polycarbonate (PC). Glass fibres. Product UL certified. Low smoke toxicity index and optical density. High dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.44 | g/cm³ | ISO 1183 |
| Molding Shrinkage 1 | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.35 to 0.55 | % | |
| Flow : 2.00 mm | 0.15 to 0.35 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ISO 527-2/1 | ||
| 23°C | 8000 | MPa | |
| 60°C | 7500 | MPa | |
| 90°C | 7000 | MPa | |
| 120°C | 6200 | MPa | |
| Tensile Stress | ISO 527-2/5 | ||
| Break, 23°C | 100 | MPa | |
| Break, 60°C | 85.0 | MPa | |
| Break, 90°C | 70.0 | MPa | |
| Break, 120°C | 50.0 | MPa | |
| Tensile Strain | ISO 527-2/5 | ||
| Break, 23°C | 1.7 | % | |
| Break, 60°C | 1.4 | % | |
| Break, 90°C | 1.5 | % | |
| Break, 120°C | 1.5 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -20°C | 6.8 | kJ/m² | |
| 23°C | 7.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| -20°C | 30 | kJ/m² | |
| 23°C | 30 | kJ/m² | |
| Notched Izod Impact (23°C, 3.20 mm) | 80 | J/m | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 140 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 135 | °C | ISO 75-2/A |
| Continuous Use Temperature 2 | 135 | °C | |
| Vicat Softening Temperature | 145 | °C | ISO 306/B50 |
| CLTE - Flow (30 to 100°C) | 1.0E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index 3(Solution A) | 150 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-1 | UL 94 | |
| Oxygen Index | 31 | % | ASTM D2863 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 to 130 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 270 to 290 | °C | |
| Mold Temperature | 100 to 120 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | at 60 Mpa of cavity pressure |
| 2 . | 20,000 hr |
| 3 . | Without Surfactant |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| PRL PC-UV3-D(f1) | Polymer Resources Ltd. | PC | PRL |
| Quadrant EPP Semitron® ESd 410C | Quadrant Engineering Plastic Products | PEI | Quadrant EPP |
| SEQUEL® 1980-PUV | LyondellBasell Industries | TPO (POE) | SEQUEL® |
| Sylvin 9728-45 Black | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Unipren® Elastomers A3 CRLA010 35A EG06IN4 UP332 | Petropol Industry and Trade of Polymers LTDA | TPE | Unipren® Elastomers |