SABIC® PP 527K
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d30IIr_SABIC-PP-527K.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP 527K is a leading grade typically used for products in thermoforming. Tailoring of the polymer architecture combined with effective nucleation resulted in a good balance of very high stiffness combined with excellent transparency. Its high crystallisation temperature is ideally suited for further line speed improvements. Moreover it is formulated with a combined processing and antistatic additive package. Application: SABIC® PP 527K is typically used in packaging for Fruit, Vegetables, Meat, Fish, Poultry and Ambient Food packaging. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 3.0 | g/10 min | ASTM D1238, ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 2300 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 40.0 | MPa | ASTM D638 |
| Yield | 40.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 6.0 | % | ASTM D638 |
| Yield | 6.0 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.5 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 30 | J/m | ASTM D256A |
| 23°C | 3.0 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 120 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 115 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 70.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 65.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 155 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 100 | °C | ASTM D1525, ISO 306/B120 7 7 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NYLEM® 6 HV | EMAS Plastik San.Tic.AS. | Nylon 6 | NYLEM® |
| Clariant Nylon 6/6 6601-FR | Clariant Corporation | Nylon 66 | Clariant Nylon 6/6 |
| Sylvin 83001-50 Red 6238 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Cellasto® MH24-60 | BASF Polyurethanes GmbH | TPU, Unspecified | Cellasto® |
| Neoflex™ 8055 | Zylog Plastalloys Pvt. Ltd. | TPE | Neoflex™ |