Ixef® 1524
| Category: | PARA , Polyarylamide |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Ixef® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d2qI2Y_Ixef-1524.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ixef 1524 is a 50% glass fiber reinforced, halogen-free flame retardant polyacrylamide with high strength, high rigidity, good surface gloss and excellent creep resistance. -black: Ixef 1524/9008 -customers can color by themselves |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.68 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | 0.10 - 0.30 | -- | % | Internal method |
| Water Absorption | ||||
| 23°C, 24 hr | 0.30 | -- | % | ISO 62 |
| Balance, 50% RH | 1.0 | -- | % | Internal method |
| Equilibrium, 65% RH | 1.3 | -- | % | Internal method |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 20000 | -- | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 230 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break) | 1.9 | -- | % | ISO 527-2 |
| Flexural Modulus | 18500 | 15500 | MPa | ISO 178 |
| Flexural Stress | 330 | 240 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | 9.3 | -- | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | 48 | -- | kJ/m² | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 227 | -- | °C | ISO 75-2/A |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Dielectric Constant 1(2.40 GHz) | 4.44 | -- | ASTM D2520 | |
| Dissipation Factor 2(2.40 GHz) | 0.012 | -- | ASTM D2520 | |
| Comparative Tracking Index (CTI) (3.00 mm) | > 600 | -- | V | UL 746 |
| Comparative Tracking Index (CTI) (3.00 mm) | PLC 0 | -- | UL 746 | |
| Comparative Tracking Index | > 600 | -- | V | IEC 60112 |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.400 mm | 37.6 | -- | UL 746 | |
| 0.750 mm | 53.6 | -- | UL 746 | |
| 1.50 mm | 70.2 | -- | UL 746 | |
| 3.00 mm | 95.4 | -- | UL 746 | |
| High Amp Arc Ignition (HAI) | UL 746 | |||
| 0.400 mm | PLC 2 | -- | UL 746 | |
| 0.750 mm | PLC 2 | -- | UL 746 | |
| 1.50 mm | PLC 1 | -- | UL 746 | |
| 3.00 mm | PLC 1 | -- | UL 746 | |
| High Voltage Arc Resistance to Ignition (HVAR) (3.00 mm) | PLC 0 | -- | UL 746 | |
| High Voltage Arc Tracking Rate (HVTR) (3.00 mm) | PLC 0 | -- | UL 746 | |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.400 mm | 95 | -- | sec | UL 746 |
| 0.750 mm | > 120 | -- | sec | UL 746 |
| 1.50 mm | > 120 | -- | sec | UL 746 |
| 3.00 mm | > 120 | -- | sec | UL 746 |
| Hot-wire Ignition (HWI) | UL 746 | |||
| 0.400 mm | PLC 1 | -- | UL 746 | |
| 0.750 mm | PLC 0 | -- | UL 746 | |
| 1.50 mm | PLC 0 | -- | UL 746 | |
| 3.00 mm | PLC 0 | -- | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating 3(mm, colored) | V-0 | -- | UL 94 | |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | |||
| 0.400 mm | 775 | -- | °C | IEC 60695-2-13 |
| 0.750 mm | 800 | -- | °C | IEC 60695-2-13 |
| 1.50 mm | 825 | -- | °C | IEC 60695-2-13 |
| 3.00 mm | 850 | -- | °C | IEC 60695-2-13 |
| Oxygen Index | 37 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 100 | °C | |
| Drying Time | 1.0 - 3.0 | hr | |
| Rear Temperature | 250 - 260 | °C | |
| Front Temperature | 260 - 290 | °C | |
| Processing (Melt) Temp | 280 | °C | |
| Mold Temperature | 120 - 140 | °C |
| Injection instructions |
|---|
| 热流道系统：250 °C～260 °C （ 482°F～500 °F ） 射出压力：快速 干燥： 该树脂应该干燥～要求的0.10% 含湿率。 如果使用的除湿空气干燥机露点为-28 ° C（ -18 °F ）或更低，应遵循以下规则：120 ° C（248 °F）温度下 1〜2小时， 100℃ C（ 212°F）温度下2〜4小时，或80 ℃（176 °F）温度下2-8小时。 注塑成型： IXEF1524混合物在大多数螺杆注塑机上均可以很容易地注射成型。建议采用通用螺杆，背压尽可能低。 测得的熔融温度应该在270℃ （518° F）左右，机筒后端温度应该在250～260℃ （ 482～500°F ）左右，前端逐渐增至260 ℃〜275℃ （500～527 °F）。如果使用热流道，温度应设置为250～260 ℃（482～500 ° F ） 。 为了最大限度地提高结晶度，模腔表面温度必须保持在120～140℃（ 248～284°F）之间。成型温度低，容易使产品产生翘曲、外观不良，并极可能产生蠕变。射出压力应确保快速射出。调整保压压力和时间，尽量提高零件的重量。部件正好完全填充完毕（ 95-99％）前，将注塑件从射出部位转移到螺杆位置进行保压。 |
| Note Message | |
|---|---|
| 1 . | Method B |
| 2 . | Method B |
| 3 . | These flammability ratings do not represent the risk of these materials or any other materials in actual fire situations. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SAXALEN™ PPH327G28 | SAX Polymers | PP Homopolymer | SAXALEN™ |
| 3M™ Dyneon™ TFM™ Modified PTFE Compound TFM 4216 | 3M Advanced Materials Division | PTFE | 3M™ Dyneon™ TFM™ Modified PTFE Compound |
| ETILINAS HD5739UB | POLYETHYLENE MALAYSIA SDN BHD | HDPE | ETILINAS |
| FHR Polypropylene AP5325-HS | Flint Hills Resources, LP | PP Impact Copolymer | FHR Polypropylene |
| Macromeric® 0103-212a NT | Saco Polymers | Polyolefin, Unspecified | Macromeric® |