Badadur® PBT8 FR HF
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Bada AG |
| Trademark: | Badadur® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d2n31g_Badadur-PBT8-FR-HF.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Medium viscosity, non halogenated flame retardent standard injection moulding grade with very good mechanical properties |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.45 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| Saturation, 23°C | 0.42 | % | |
| Equilibrium, 23°C, 50% RH | 0.17 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus 1(23°C) | 2700 | MPa | ISO 527-2/1 |
| Tensile Stress 2(Break, 23°C) | 45.0 | MPa | ISO 527-2/5 |
| Tensile Strain (Break, 23°C, 5.00 mm) | 4.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 3 | ISO 179/1eA | ||
| -30°C | 3.0 | kJ/m² | |
| 23°C | 5.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 4 | |||
| 0.45 MPa, Unannealed | 160 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 60.0 | °C | ISO 75-2/A |
| Melting Temperature (DSC) 5 | 223 | °C | ISO 3146 |
| CLTE | DIN 53752 | ||
| Flow 6 | 1.3E-4 | cm/cm/°C | |
| Transverse 7 | 1.3E-4 | cm/cm/°C | |
| Maximum Service Temperature | IEC 216 | ||
| 20000 hrs | 130 | °C | |
| some hours | 155 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity 8 | 1.0E+14 | ohms | IEC 60093 |
| Volume Resistivity 9 | 1.0E+16 | ohms·cm | IEC 60093 |
| Relative Permittivity 10(1 MHz) | 3.50 | IEC 60250 | |
| Dissipation Factor 11(1 MHz) | 0.018 | IEC 60250 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating 12(1.60 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 to 130 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 240 to 260 | °C | |
| Mold Temperature | 60.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | Test Specimen accordng to ISO 3167, Type A |
| 2 . | Test Specimen accordng to ISO 3167, Type A |
| 3 . | 80x10x4 mm |
| 4 . | 110x10x4 |
| 5 . | 10 K/min, Compound for moulding |
| 6 . | >= 10x10x4 |
| 7 . | > = 10x10x4 |
| 8 . | 80x80x1 mm |
| 9 . | 80x80x1 mm |
| 10 . | 80x80x1 mm |
| 11 . | 80x80x1 mm |
| 12 . | 125x13x1.6 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2900-80 Clear | Sylvin Technologies Incorporated | PVC, Flexible | Sylvin |
| Bergamid™ B700 Mi10 UF | PolyOne Corporation | Nylon 6 | Bergamid™ |
| LIHAN® A801 | Nanjing Lihan Chemical Co., Ltd. | Nylon 66 Alloy | LIHAN® |
| Petrothene® NA272130 | LyondellBasell Industries | MDPE | Petrothene® |
| ULTEM™ HU1000 resin | SABIC Innovative Plastics | PEI | ULTEM™ |