EPO-TEK® T7109-20
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Epoxy Technology Inc. |
| Trademark: | EPO-TEK® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | d2UXV2_EPO-TEK-T7109-20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Flexible thermally conductive epoxy. A more flexible version of EPO-TEK® T7109-19. |
| General Information | |
|---|---|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Physical | Nominal Value | Unit | |
|---|---|---|---|
| Particle Size | < 20.0 | µm |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Degradation Temperature | 307 | °C | |
| Die Shear Strength - <5 kg (23°C) | 11.7 | MPa | |
| Operating Temperature | |||
| Continuous | -55 to 150 | °C | |
| Intermittent | -55 to 250 | °C | |
| Storage Modulus | 17.2 | MPa | |
| Thixotropic Index | 2.80 | ||
| Weight Loss on Heating | |||
| 200°C | 0.21 | % | |
| 250°C | 0.51 | % | |
| 300°C | 1.8 | % |
| Thermal | Nominal Value | Unit | |
|---|---|---|---|
| Glass Transition Temperature 1 | < 20.0 | °C | |
| CLTE - Flow | |||
| -- 2 | 5.2E-5 | cm/cm/°C | |
| -- 3 | 2.3E-4 | cm/cm/°C | |
| Thermal Conductivity | 0.92 | W/m/K |
| Thermoset | Nominal Value | Unit | |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 10 | ||
| Part B | Mix Ratio by Weight: 1.5 | ||
| Shelf Life (23°C) | 52 | wk |
| Uncured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Color | |||
| -- 4 | Clear/Transparent | ||
| -- 5 | Grey | ||
| Density | |||
| Part B | 1.02 | g/cm³ | |
| Part A | 1.35 | g/cm³ | |
| Viscosity 6(23°C) | 30 to 60 | Pa·s | |
| Curing Time (80°C) | > 2.0 | hr | |
| Pot Life | 90 | min |
| Cured Properties | Nominal Value | Unit | |
|---|---|---|---|
| Shore Hardness (Shore A) | 78 | ||
| Lap Shear Strength (23°C) | 5.36 | MPa | |
| Relative Permittivity (1 kHz) | 4.10 | ||
| Volume Resistivity (23°C) | > 2.0E+11 | ohms·cm | |
| Dissipation Factor (1 kHz) | 0.074 |
| Note Message | |
|---|---|
| 1 . | Dynamic Cure 20-200°C/ISO 25 Min; Ramp -10-200°C @ 20°C/Min |
| 2 . | Below Tg |
| 3 . | Above Tg |
| 4 . | Part B |
| 5 . | Part A |
| 6 . | 5 rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Utomer UT880 | Shanghai Utomer Material Science Co., Ltd. | TPU-Polyether | Utomer |
| ECP 121/1015 | TBA Electro Conductive Products Ltd. | EVA | ECP |
| Kotex KGN-30MRA | Kotec Corporation | PC | Kotex |
| Karina CLEAR PVC COMPOUND -E 80/202-D-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| OP - PC/ABS 604-I-FR | Oxford Polymers | PC+ABS | OP - PC/ABS |