Amodel® AS-1933 HS Datasheet,PPA,Solvay Specialty Polymers-SHANGHAI SUSHENG

Message
AMODEL AS -1933 HS is a 33% glass fiber reinforced grade polyphthalamide (PPA) resin specially developed to improve the performance of products in 50/50 ethylene glycol and water environment. When exposed to anti-freezing agents at 226 °F(108 ℃) or even at 275 °F(135 ℃) test temperatures, the performance of this material exceeds the requirements of the automotive industry for polymer materials. It can be used in various auto parts, such as thermostat housing, heater core end cap, heater hose connector and water inlet, power socket and valve lamp. -black: AS-1933 HS BK 324

General Information
Filler / Reinforcement	Glass fiber reinforced material, 33% filler by weight
Additive	heat stabilizer
Features	Good dimensional stability Rigid, good High strength frost resistance Good creep resistance Good chemical resistance Heat resistance, high Ethylene glycol resistance Thermal Stability
Uses	Power/other tools Valve/valve components Industrial components Industrial application Thick wall fittings (parts) Machine/mechanical parts Metal substitution Parts under the hood of a car Application in Automobile Field Shell
RoHS Compliance	RoHS compliance
Appearance	Black
Forms	Particle
Processing Method	Injection molding
Multi-Point Data	Isothermal Stress vs. Strain (ISO 11403-1) Secant Modulus vs. Strain (ISO 11403-1)

Physical	Nominal Value	Unit	Test Method
Density	1.45	g/cm³	ISO 1183/A
Molding Shrinkage			ASTM D955
Flow	0.20	%	ASTM D955
Transverse flow	0.60	%	ASTM D955
Water Absorption (24 hr)	0.21	%	ASTM D570

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
-- ¹	7580	MPa	ASTM D638
--	11700	MPa	ASTM D638
--	12600	MPa	ISO 527-2
Tensile Strength
Fracture ²	75.8	MPa	ASTM D638
Fracture	221	MPa	ASTM D638
Fracture	212	MPa	ISO 527-2
Tensile Elongation (Break)	2.5	%	ASTM D638, ISO 527-2
Flexural Modulus
--	10800	MPa	ASTM D790
--	10600	MPa	ISO 178
Flexural Stress
--	309	MPa	ISO 178
Yield	313	MPa	ASTM D790

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength	10	kJ/m²	ISO 179/1eA
Charpy Unnotched Impact Strength	76	kJ/m²	ISO 179/1eU
Notched Izod Impact
-- ³	53	J/m	ASTM D256
--	91	J/m	ASTM D256
--	9.5	kJ/m²	ISO 180/1A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
1.8 MPa, not annealed	277	°C	ASTM D648
1.8 MPa, not annealed	278	°C	ISO 75-2/Af
Melting Temperature	312	°C	ISO 11357-3

Injection	Nominal Value	Unit
Drying Temperature	121	°C
Drying Time	4.0	hr
Suggested Max Moisture	0.10	%
Hopper Temperature	79.4	°C
Rear Temperature	304 - 318	°C
Front Temperature	316 - 329	°C
Processing (Melt) Temp	321 - 343	°C
Mold Temperature	135	°C

Injection instructions
Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Injection instructions

Storage: Amodel® compounds are shipped in moisture-resistant packages at moisture levels according to specifications. Sealed, undamaged bags should be preferably stored in a dry room at a maximum temperature of 50°C (122°F) and should be protected from possible damage. If only a portion of a package is used, the remaining material should be transferred into a sealable container. It is recommended that Amodel® resins be dried prior to molding following the recommendations found in this datasheet and/or in the Amodel® processing guide.

Note Message
1 .	Impregnate in 50/50 ethylene glycol/water mixture at 275 °F(135°C) for 1000 hours
2 .	Impregnate in 50/50 ethylene glycol/water mixture at 275 °F(135°C) for 1000 hours
3 .	Impregnate in 50/50 ethylene glycol/water mixture at 275 °F(135°C) for 1000 hours

Category:	PPA , Polyphthalamide
Manufacturer:	Solvay Specialty Polymers
Trademark:	Amodel®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	d17Z1p_Amodel-AS-1933-HS.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Tenogel® ABS A3 LF NTLA010 AB348	Petropol Industry and Trade of Polymers LTDA	ABS	Tenogel® ABS
ULTEM™ AR9200 resin	SABIC Innovative Plastics	PEI	ULTEM™
DENKA POVAL K-24E	Denka Company Limited	PVOH	DENKA POVAL
ELIX™ 5130	ELIX Polymers, S. L.	PC+ABS	ELIX™
POTICON BT262	Otsuka Chemical Co., Ltd.	PBT	POTICON