Kepamid® 1310GSU

Category:	Nylon 6 , Polyamide 6
Manufacturer:	Korea Engineering Plastics Co., Ltd
Trademark:	Kepamid®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	czZuX2_Kepamid1310GSU.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

KEPAMID 1310GSU is a GF 8%-reinforced, impact-modified, and UV-stabilized PA6 grade.

It features strong mechanical properties, impact strength, and UV and heat resistance.

It is suitable for applications such as automotive, electrical & electronics, and industrial parts.

General Information
Filler / Reinforcement	Glass fiber reinforced material, 8.0% filler by weight
Additive	Impact modifier UV stabilizer
Features	Good Heat Resistance UV Stabilized Impact modification Impact resistance, good Good UV resistance
Uses	Electrical/Electronic Applications Industrial components Application in Automobile Field
RoHS Compliance	RoHS compliance
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.15	g/cm³	ISO 1183
shrinkage- Flow (3.00 mm)	0.60 - 0.70	%	Internal method
Water Absorption (Equilibrium, 23°C, 50% RH)	1.5	%	ISO 62

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	112		ISO 2039-2

Mechanical	Nominal Value	Unit	Test Method
Tensile Stress	77.0	MPa	ISO 527-2
Tensile Strain (Break)	4.0	%	ISO 527-2
Flexural Modulus	3300	MPa	ISO 178
Flexural Stress	110	MPa	ISO 178

Impact	Nominal Value	Unit	Test Method
Charpy Notched Impact Strength (23°C)	7.5	kJ/m²	ISO 179/1eA

Thermal	Nominal Value	Unit	Test Method
Heat Deflection Temperature
0.45 MPa, not annealed	205	°C	ISO 75-2/B
1.8 MPa, not annealed	190	°C	ISO 75-2/A
Melting Temperature ¹	220	°C	ISO 11357-3

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	1.0E+15	ohms·cm	IEC 60093
Relative Permittivity (1 MHz)	3.80		IEC 60250

Flammability	Nominal Value	Unit	Test Method
Flame Rating (0.8 mm)	HB		UL 94

Injection	Nominal Value	Unit
Drying Temperature
--	90	°C
Dry Air Dryer	80	°C
Drying Time
--	6.0 - 8.0	hr
Dry Air Dryer	4.0 - 6.0	hr
Suggested Max Moisture	0.050	%
Hopper Temperature	60 - 80	°C
Rear Temperature	250	°C
Middle Temperature	260	°C
Front Temperature	260	°C
Nozzle Temperature	260	°C
Mold Temperature	70 - 90	°C
Back Pressure	0.490 - 0.981	MPa
Screw Speed	80 - 120	rpm

Note Message
1 .	10°C/min

Resin Grade	Manufacturer	Category	Trademark
Spartech Polycom PP6140 A2	Spartech Polycom	PP, Unspecified	Spartech
Sylvin 8203-55 Natural	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
Eastar™ EN058, Natural	Eastman Chemical Company	Copolyester	Eastar™
DynaPath™ 1462X	Polymer Dynamix	PBT	DynaPath™
ESTABLEND 4500 V0 HF	Cossa Polimeri S.r.l.	PC+ABS	ESTABLEND