LUVOCOM® 6-8826 Datasheet,Nylon 12,Lehmann & Voss & Co.-SHANGHAI SUSHENG

Message
LUVOCOM®6-8826 is a polyamide 12 (nylon 12) material,. This product is available in Europe,. LUVOCOM®The main features of 6-8826 are: Conductivity Electrostatic protection moisture resistance Typical application areas include: textile/fiber engineering/industrial accessories Automotive Industry business/office supplies

General Information
Features	Conductivity Electrostatic discharge protection Good liquidity Low or no water absorption
Uses	Textile applications Engineering accessories Application in Automobile Field Business equipment
Appearance	Natural color

Physical	Nominal Value	Unit	Test Method
Density	4.52	g/cm³	ISO 1183
Molding Shrinkage	0.50 - 0.90	%	DIN 16901
Water Absorption (23°C, 24 hr)	< 0.10	%

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus	12000	MPa	ISO 527-2
Tensile Stress (Break)	70.0	MPa	ISO 527-2
Tensile Strain (Yield)	2.1	%	ISO 527-2
Flexural Modulus	10000	MPa	ISO 178
Flexural Stress	90.0	MPa	ISO 178
Flexural Strain at Flexural Strength	2.7	%	ISO 178

Thermal	Nominal Value	Unit	Test Method
Maximum operating temperature- Short Term	140	°C

Electrical	Nominal Value	Unit	Test Method
Insulation Resistance		ohms	IEC 60167

Impact	Nominal Value	Unit	Test Method
Charpy Unnotched Impact Strength (23°C)	25	kJ/m²	ISO 179/1eU

Thermal	Nominal Value	Unit	Test Method
Continuous Use Temperature	90.0	°C	UL 746B

Electrical	Nominal Value	Unit	Test Method
Surface Resistivity	< 10	ohms	IEC 60093

Injection	Nominal Value	Unit
Drying Temperature
A	75.0	°C
B	105	°C
Drying time- A	6.0 - 10	hr
Suggested Max Moisture	0.10	%
Rear Temperature	230 - 250	°C
Middle Temperature	240 - 260	°C
Front Temperature	250 - 270	°C
Nozzle Temperature	250 - 260	°C
Processing (Melt) Temp	250	°C
Mold Temperature	70.0 - 110	°C

Injection instructions
General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Injection instructions

General In general LUVOCOM® can be processed on conventional injection moulding machines while observing the usual technical guidelines. Any added fibrous materials or fillers may have an abrasive effect. In this case the cylinder and screw should be protected against wear as is usual in the processing of reinforced thermoplastic materials. Lengthy dwell times for the melts in the cylinder should be avoided. Lower the temperatures during interruptions! Predrying (optional) It is advisable to predry the granulate with a suitable dryer immediately before processing. The granulate may absorb moisture from the air. Delivery Form & Storage Unless indicated otherwise, the material is delivered as 3mm-long pellets in sealed bags on pallets. Preferably storage should be effected in dry and normally temperatured rooms Additional Information During processing the moisture level should not exceed 0.1%, otherwise molecular degradation and surface defects (e.g. smearing) may occur. As the material absorbs water rapidly, originally sealed containers should only be opened immediately before processing. Excessively high predrying temperatures may cause discoloration. The processing notes provided merely represent a recommendation for general use. Due to the large variety of machines, geometries and volumes of parts, etc., it may be necessary to employ different settings according to the specific application. Please contact us for further information.

Category:	Nylon 12 , Polyamide 12
Manufacturer:	Lehmann & Voss & Co.
Trademark:	LUVOCOM®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	cyc4pc_LUVOCOM-6-8826.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
QR Resin QR-8000-GFR30	QTR, Inc.	PBT	QR Resin
Retpol® 6019	PolyPacific Pty. Ltd.	PP Homopolymer	Retpol®
ColorRx® PE2-1800RX	LTL Color Compounders, Inc.	PE Copolymer	ColorRx®
GETILAN MAC/900	Crosspolimeri S.p.A.	LDPE	GETILAN
LNP™ THERMOCOMP™ Noryl_HM3020 compound	SABIC Innovative Plastics Europe	PPE+PS	LNP™ THERMOCOMP™