TAROMID A 280 Z1
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Taro Plast S.p.A. |
| Trademark: | TAROMID A |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cyG8SI_TAROMID-A-280-Z1.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
TAROMID A 280 Z1 is a polyamide 66 (nylon 66) product,. It can be processed by injection molding and is available in Europe. Features include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.11 - 1.13 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (280°C/1.0 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 1.5 - 1.7 | % | Internal method |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.2 | % | ISO 62 |
| Saturated, 23°C | 7.0 | % | ISO 62 |
| Granule Humidity 1 | % | Internal method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 60.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 50 | % | ISO 527-2/50 |
| Flexural Modulus 2 | 2500 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 100 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature 3(1.8 MPa, Unannealed) | 75.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 225 | °C | ISO 306/B50 |
| Ball Pressure Test (165°C) | Pass | IEC 60695-10-2 | |
| Melting Temperature | 256 | °C | ISO 11357-3 |
| CLTE - Flow (-30 to 30°C) | 7.0E-5 - 1.0E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 3.0E+15 | ohms·cm | IEC 60093 |
| Dielectric Constant | 3.80 | IEC 60250 | |
| Comparative Tracking Index (Solution A) | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (0.970 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 80.0 - 90.0 | °C | |
| Hot air dryer | 80.0 - 100 | °C | |
| Drying Time | |||
| -- | 1.0 | hr | |
| Hot air dryer | 3.0 | hr | |
| Processing (Melt) Temp | 250 - 270 | °C | |
| Mold Temperature | 70.0 - 80.0 | °C | |
| Injection Rate | Moderate-Fast |
| Injection instructions |
|---|
| Pre-heat Temperature: 80 to 100°CPre-heat Time: 3 hr |
| Note Message | |
|---|---|
| 1 . | TARO 002 |
| 2 . | 1.0 mm/min |
| 3 . | 120°C/hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| THERMOLAST® K TC9FRN (Series: FR) | KRAIBURG TPE | TPE | THERMOLAST® K |
| Vital-Line SHE1200XT | Teknor Apex Asia Pacific PTE. LTD. | PVC, Flexible | Vital-Line |
| Axiall PVC 18841 | Axiall Corporation | PVC, Flexible | Axiall PVC |
| LubriOne™ PC-20CF/15T | PolyOne Corporation | PC | LubriOne™ |
| Plaskon MUF-2A LAR | Cookson Electronics - Semiconductor Products | Epoxy | Plaskon |