Elastollan® B 60 A 12 ESD 000
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | BASF Polyurethanes GmbH |
| Trademark: | Elastollan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cy7DYo_ElastollanB60A12ESD000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Thermoplastic Polyester-Polyurethane with excellent mechanical properties, outstanding wear resistance, high tear and tensile strength, good damping characteristic, high resilience performance and superior low temperature flexibility. |
| General Information | |
|---|---|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.17 | g/cm³ | ISO 1183/A |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 3 sec) | 63 | ISO 7619 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Abrasion Loss | 60.0 | mm³ | ISO 4649-A |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | DIN 53504-S2 | ||
| 20% strain | 1.00 | MPa | DIN 53504-S2 |
| 100% strain | 2.50 | MPa | DIN 53504-S2 |
| 300% strain | 6.50 | MPa | DIN 53504-S2 |
| Tensile Stress | DIN 53504-S2 | ||
| Yield | 30.0 | MPa | DIN 53504-S2 |
| Yield 1 | 25.0 | MPa | DIN 53504-S2 |
| Tensile Elongation | DIN 53504-S2 | ||
| Fracture | 800 | % | DIN 53504-S2 |
| Fracture 2 | 900 | % | DIN 53504-S2 |
| Tear Strength 3 | 50 | kN/m | ISO 34-1 |
| Compression Set | ISO 815 | ||
| 23°C, 72 hr | 20 | % | ISO 815 |
| 70°C, 24 hr | 30 | % | ISO 815 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | No Break | ISO 179 | |
| 23°C | No Break | ISO 179 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 5.0E+7 | ohms·cm | IEC 60093 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80 - 90 | °C | |
| Drying Time | 2.0 - 3.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Hopper Temperature | 40 | °C | |
| Rear Temperature | 180 - 190 | °C | |
| Middle Temperature | 185 - 200 | °C | |
| Front Temperature | 190 - 200 | °C | |
| Nozzle Temperature | 195 - 205 | °C | |
| Processing (Melt) Temp | 190 - 200 | °C | |
| Mold Temperature | 20 - 40 | °C | |
| Injection Rate | Slow | ||
| Back Pressure | 5.00 - 15.0 | MPa | |
| Screw L/D Ratio | 18.0:1.0 to 22.0:1.0 | ||
| Screw Compression Ratio | 2.0 : 1.0 - 3.0 : 1.0 |
| Note Message | |
|---|---|
| 1 . | after storage in water for 21 days at 80°C |
| 2 . | after storage in water for 21 days at 80°C |
| 3 . | Method B, right-angle specimen (cut) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ultramid® A3X3G5 | BASF Corporation | Nylon 66 | Ultramid® |
| Fainplast PVC KL 92/1 | Fainplast Compounds S.r.l | PVC, Unspecified | Fainplast PVC |
| INELEC PPCF10 | Infinity LTL Engineered Compounds | PP, Unspecified | INELEC |
| ISPLEN® PP 030 G1E | REPSOL | PP Homopolymer | ISPLEN® |
| Polifil® PP RMC-20V | The Plastics Group | PP, Unspecified | Polifil® PP |