EPLAMID 6 GFR 10 NC
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | EPSAN Plastik SAN. ve TiC. A.S. |
| Trademark: | EPLAMID 6 |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cxaate_EPLAMID-6-GFR-10-NC.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polyamide 6, reinforced with 10% of glass fiber, heat stabilized, lubricated for injection moulding. Eplamid 6 GFR 10 is used in all sectors of industry, offering a perfect balance of thermal and mechanical properties. This material is available in natural and in colours on request. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.16 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | |||
| Vertical flow direction : 3.00mm | 1.1 | -- | % | ISO 294-4 |
| Flow direction : 3.00mm | 0.80 | -- | % | ISO 294-4 |
| Moisture Content | 0.20 | -- | % | ISO 15512 |
| Ash Content | 10 | -- | % | ISO 3451-4 |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Durometer Hardness (Shore D, 23°C) | 82 | -- | ISO 868 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 4200 | 3700 | MPa | ISO 527-2/50 |
| Tensile Stress (Break, 23°C) | 115 | 90.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break, 23°C) | 3.0 | 6.0 | % | ISO 527-2/50 |
| Flexural Modulus 1(23°C) | 3900 | 3500 | MPa | ISO 178 |
| Flexural Stress 2(23°C) | 190 | 170 | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 8.0 | 10 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 7.0 | 9.0 | kJ/m² | ISO 180/1A |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature 3 | ||||
| 0.45 MPa, not annealed | 208 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 205 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 210 | -- | °C | ISO 306/B120 |
| Melting Temperature (DSC) | 215 | -- | °C | ISO 3146 |
| Flammability | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| Flame Rating (1.60 mm) | HB | -- | UL 94, IEC 60695-11-10, -20 |
| Additional Information |
|---|
| 干燥 TEST CONDITIONS: Laboratory conditions are 23 ±2°C and 45-55 % RH. |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Processing (Melt) Temp | 260 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| 3 . | 120°C/h |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RELENE® EE20 | Reliance Industries Limited | HDPE | RELENE® |
| Akulon® K224-TG9/A | DSM Engineering Plastics | Nylon 6 | Akulon® |
| Geon™ SF M7020 | PolyOne Corporation | PVC, Rigid | Geon™ SF |
| Karina BLACK PVC COMPOUND 510-DA-48/1-Y-IS-BZ (***) | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Osterlene® PPC-100-1.1 | Osterman & Company | PP Copolymer | Osterlene® |