Order Products : sales@su-jiao.com
AEI SX738:CM424
| Category: | XLPE , Crosslinked Polyethylene |
| Manufacturer: | AEI Compounds Limited |
| Trademark: | AEI |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cxO5At_AEI-SX738-CM424.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Low-smoke, low-toxicity, halogen-free, flame retardant, silane crosslinkable compound for the production of flexible heat shrinkable tubing. SX738 is a low smoke, low fume, fire retardant silane grafted compound, curable by exposure to moist conditions. This is designed specifically for the production, by extrusion, of flame retardant halogen free heat shrinkable tubing. The graft component SX738 is mixed with a crosslinking catalyst masterbatch CM424 generally in the ratio 95:5. The two component system SX738:CM424 combines ease of processing with the ability to achieve a degree of crosslinking compatible with good expansion and contraction. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.40 | g/cm³ | BS 2782 620A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | 10.0 | MPa | IEC 60811-1-1 |
| Tensile Strain (Break) | 200 | % | IEC 60811-1-1 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength (135°C, 168 hr) | < 25 | % | IEC 60811-1-2 |
| Change in Tensile Strain at Break (135°C, 168 hr) | < 25 | % | IEC 60811-1-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Temperature index | > 200 | °C | ISO 4589-3 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Conduction rate- of gases | 13.0 | µS/cm | IEC 60754-2 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Corrosive gases in flue gas- pH | 4.60 | IEC 60754-2 | |
| Smoke Density | % | ASTM D2843 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Halogen Acid Gas Evolution | % | IEC 60754-1 | |
| Hot Elongation - 35 lb/mm² (150°C) | % | Internal method |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Head Temperature | 190 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+13 | ohms·cm | IEC 60502 |
| Dielectric Strength | 14 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Oxygen Index | 26 | % | ISO 4589-2 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Crosslinking or Cure: A satisfactory cure can be obtained either by immersion in hot water or exposure to low pressure steam at a temperature up to 65°C |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Cylinder Zone 1 Temp. | 130 | °C | |
| Cylinder Zone 2 Temp. | 150 | °C | |
| Cylinder Zone 3 Temp. | 170 | °C | |
| Cylinder Zone 4 Temp. | 180 | °C | |
| Die Temperature | 190 | °C |
| Extrusion instructions |
|---|
| Many modern thermoplastic extruders will process the material although a screw designed to give good homogenisation without excessive shear (which could cause unacceptable increases in melt temperature) should be used. An extruder with an L/D ratio (length/diameter) of 15-24 and an extruder screw of compression ratio 2-3:1 are recommended. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Safrene® D 7255HL | Safripol (PTY) LTD | HDPE | Safrene® |
| Ultramid® A3W R01 SW805 | BASF Corporation | Nylon 66 | Ultramid® |
| AMPLIFY™ TY 3351 | The Dow Chemical Company | MAH-g | AMPLIFY™ TY |
| ColorFast® FRPBT200 | LTL Color Compounders, Inc. | PBT | ColorFast® |
| Electroblend® ABS-2800 | Colour Image Plastic Compound Sdn. Bhd. (CIPC) | ABS | Electroblend® |