3M™ Dyneon™ PTFE Compound TF 4102
| Category: | PTFE , Polytetrafluoroethylene |
| Manufacturer: | 3M Advanced Materials Division |
| Trademark: | 3M™ Dyneon™ PTFE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cwb3Qg_3M-Dyneon-PTFE-Compound-TF-4102.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Features
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 2.20 | g/cm³ | ISO 12086 |
| Apparent Density | 0.82 | g/cm³ | ISO 12086 |
| Average Particle Size | 580 | µm | ISO 12086 |
| Additional Information | Nominal Value | Unit | |
|---|---|---|---|
| Compression Molding Molding Pressure | 40.0 | MPa | |
| Compression Molding Temperature | 23 to 26 | °C | |
| Sintering Temperature | < 365 | °C |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 1(Break) | 22.0 | MPa | ISO 12086 |
| Tensile Strain 2(Break) | 460 | % | ISO 12086 |
| Deformation Under Load 3(23°C, 15 MPa) | 11.0 | % | ASTM D621 |
| Note Message | |
|---|---|
| 1 . | Measured on sintered moldings |
| 2 . | Measured on sintered moldings |
| 3 . | 100 h load, 25 h relaxation |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® MD 12 HLMI | Marco Polo International, Inc. | MDPE | MARPOL® MD |
| Latistat 66-06 | LATI S.p.A. | Nylon 66 | Latistat |
| Karina BEIGE PVC COMPOUND -E 828-08/497-Y-RT | Karina Ind. e Com. de Pl谩sticos Ltda | PVC, Unspecified | Karina |
| K-Bin Rigid PVC KB-2007 | K-Bin, Inc. | PVC, Rigid | K-Bin Rigid PVC |
| Hifax TYC 762PLS | LyondellBasell Industries | TPO (POE) | Hifax |