Moplen RP2380
| Category: | PP Random Copolymer , Polypropylene Random Copolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Moplen |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | cvNtG3_Moplen-RP2380.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Moplen RP2380 is a random copolymer for injection moulding with nucleation and antistatic additivation. Moplen RP2380 offers a very good flowability and an excellent transparency. The main application of Moplen RP2380 is thin walled packaging with high transparency. Moplen RP2380 has a superior aesthetic appearance and can be processed at significantly lower temperatures. Moplen RP2380 enables energy savings and improved productivity due to reduced cycle times. Moplen RP2380 is a developmental grade |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.905 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 48 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/2.16 kg) | 65.0 | cm³/10min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Ball Indentation Hardness (H 358/30) | 58.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 1100 | MPa | ISO 527-2 |
| Tensile Stress (Yield) | 29.0 | MPa | ISO 527-2 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 11 | % | |
| Break | > 50 | % |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 2.5 | kJ/m² | |
| 23°C | 4.5 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 0°C | 60 | kJ/m² | |
| 23°C | 180 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 70.0 | °C | ISO 75-2/B |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ISO 306/A50 |
| -- | 72.0 | °C | ISO 306/B50 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (1000 µm) | 9.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SHIN-A SEV-3409 | SHIN-A T&C | Epoxy | SHIN-A |
| tefanyl® VR VRGR 300 | Mitsubishi Chemical Performance Polymers, Inc. | PVC, Rigid | tefanyl® VR |
| Kingfa ABP-2020 | Kingfa | PP, Unspecified | Kingfa |
| MAJORIS EWGC460H | AD majoris | PP Copolymer | MAJORIS |
| Silastic® Q7-4720 | Dow Corning Corporation | Silicone | Silastic® |