3M™ Dyneon™ Fluoroelastomer FC 2152

Category:	Fluorelastomer , Fluoroelastomer
Manufacturer:	3M Advanced Materials Division
Trademark:	3M™ Dyneon™ Fluoroelastomer
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	cvAngA_3MDyneonFluoroelastomerFC2152.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
3M™ Dyneon™ Fluoroelastomer FC 2152 is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FC 2152 has an incorporated bisphenol cure system. Special Features Composition: dipolymer of vinylidene fluoride and hexafluoropropylene Process targets: compression and transfer moulding, and calendering Excellent demoulding of complex geometric profiles Medium viscosity Proprietary incorporated cure technology Higher viscosity counterpart of 3M™ Dyneon™ Fluoroelastomer FC 2122 Typical Applications 3M™ Dyneon™ Fluoroelastomer FC 2152 is suitable for the manufacture of moulded parts with complex shapes which require an excellent demouldability.

Message

3M™ Dyneon™ Fluoroelastomer FC 2152 is a dipolymer made from hexafluoropropylene and vinylidene fluoride. FC 2152 has an incorporated bisphenol cure system.

Special Features

Composition: dipolymer of vinylidene fluoride and hexafluoropropylene

Process targets: compression and transfer moulding, and calendering

Excellent demoulding of complex geometric profiles

Medium viscosity

Proprietary incorporated cure technology

Higher viscosity counterpart of 3M™ Dyneon™ Fluoroelastomer FC 2122

Typical Applications
3M™ Dyneon™ Fluoroelastomer FC 2152 is suitable for the manufacture of moulded parts with complex shapes which require an excellent demouldability.

General Information
Features	Good demoulding performance Medium viscosity
Appearance	Opacity White-like
Forms	Thick sheet
Processing Method	Resin transfer molding Compression molding Calendering

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.80	g/cm³	Internal method
Mooney Viscosity (ML 1+10, 121°C)	51	MU	Internal method
Fluorine Content	66	%	Internal method

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A)	71		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹(100% Strain)	3.40	MPa	ASTM D412A
Tensile Strength ²	16.3	MPa	ASTM D412A
Tensile Elongation ³(Break)	330	%	ASTM D412A
Compression Set ⁴(200°C, 70 hr)	22	%	ASTM D1414

Note Message
1 .	D mould
2 .	Die D
3 .	D mould
4 .	Post cured 16 hours @ 230°C

Resin Grade	Manufacturer	Category	Trademark
Taitalac® 8540H	Taita Chemical Company, Ltd.	ABS	Taitalac®
DOW™ LLDPE DFDA-7059 NT 7	The Dow Chemical Company	LLDPE	DOW™ LLDPE
Fainplast CTX 65	Fainplast Compounds S.r.l	Polyolefin, Unspecified	Fainplast
MAJORIS FFR307C - 8487	AD majoris	PP Homopolymer	MAJORIS
TECHNYL® C 256 V18 (EX PSB 197) NATURAL	Solvay Engineering Plastics	Nylon 6	TECHNYL®