Vypet 325 is a 25 % glass/mineral reinforced PET injection molding compound designed for electrical and structural applications. Features
Typical Applications
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.50 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Vertical flow direction : 2.00mm | 0.90 | % | ISO 294-4 |
| Flow direction : 2.00mm | 0.50 | % | ISO 294-4 |
| Ash Content | 25 | % | ISO 3451-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break) | 95.0 | MPa | ISO 527-2/5 |
| Flexural Modulus 1 | 7000 | MPa | ISO 178 |
| Flexural Stress 2 | 150 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 5.0 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 6.0 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 215 | °C | ISO 75-2/A |
| Melting Temperature | 250 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 260 - 270 | °C | |
| Middle Temperature | 265 - 275 | °C | |
| Front Temperature | 270 - 295 | °C | |
| Nozzle Temperature | 275 - 300 | °C | |
| Processing (Melt) Temp | 275 - 300 | °C | |
| Mold Temperature | 95.0 - 120 | °C | |
| Injection Pressure | 55.0 - 85.0 | MPa | |
| Injection Rate | Fast | ||
| Screw Speed | 50 - 75 | rpm |
| Injection instructions |
|---|
| Back Pressure: Low |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP 40 GFC LE | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| RONFALIN® FG50 | A. Schulman Europe | ABS | RONFALIN® |
| Surlyn® 9910 | DuPont Packaging & Industrial Polymers | EMAA | Surlyn® |
| Lusin® Clean OH 251 | Chem-Trend L.P. | Unspecified | Lusin® |
| Plasmer 2065B/8901 | HYUNDAI EP Co., Ltd. | TPE | Plasmer |